Abstract:The emission of NOx can causes serious environmental pollution and endangers human health. In recent years, the selective catalytic reduction of NO with NH3 (NH3‐SCR) technology has been widely studied and adopted to reduce the production and emissions of NOx during many technologies. A series of Mn–Ce–Cox/Ti–C,N catalysts were prepared by the impregnation method, and low‐temperature NH3–SCR was studied. The results show that support modification (Ti–C,N) can broaden the operation temperature window of the catalyst (NO conversion >95%: Mn–Ce/TiO2 catalyst, 160–320 °C; Mn–Ce/Ti–C,N catalyst, 140–320 °C). The doping of Co further improves the low‐temperature NH3‐SCR of the catalyst. When n(Co):n(Ti) = 0.05, the catalyst has the best catalytic performance with the NO conversion reaches 100% at 100 °C. Temperature‐programmed reduction (H2‐TPR) and temperature‐programmed desorption (NH3‐TPD) results showed that Ti–C,N can improve the redox ability but reduces the surface acidity. Co‐doping has no effect on surface acidity, but the redox ability is further improved. A suitable amount of Co‐doping is beneficial to the optimal catalytic activity of Mn–Ce–Co0.05/Ti–C,N catalyst. This suggests a balance between redox properties and surface acidity. Especially for the strong redox ability, it can promote the oxidation of NO to NO2, and promote low‐temperature NH3‐SCR through the ‘fast SCR’ pathway. X‐ray photoelectron spectroscopy results of the highest chemisorbed oxygen (Oα) concentration and relative atomic ratio (Mn4+/Mnn+, Ce3+/Cen+ and Co3+/Con+) confirmed the above conclusion. Both the Langmuir–Hinshelwood (L‐H) and Eley–Rideal (E‐R) mechanisms occurred in the NH3‐SCR reaction over the Mn–Ce–Co0.05/Ti–C,N catalyst. © 2021 Society of Chemical Industry

A novel MnCoOx@TiO2 double–wall nanocages derived from Prussian blue analogue for NH3-SCR of NOx

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

Mnox/Ceo2/Sio2 Catalysts Prepared by Adsorption Phase Reaction Technique for Selective Catalytic Reduction of Nox at Low-Temperature

Synthesis of novel Co(3-x)MnxO4@TiO2 core-shell catalyst for low-temperature NH3-SCR of NOx with enhanced SO2 tolerance

C,N‐modified TiO2‐supported Mn–Ce–Cox‐based Catalyst for Low‐temperature NH3‐SCR

Synthesis of CrOx/C Catalysts for Low Temperature NH3-SCR with Enhanced Regeneration Ability in the Presence of SO2

Titania-Samarium-Manganese Composite Oxide for the Low-Temperature Selective Catalytic Reduction of NO with NH3

Novel Mn-Ce-Ti Mixed-Oxide Catalyst for the Selective Catalytic Reduction of NOx with NH₃.

Low Temperature Selective Catalytic Reduction of NO over Manganese Supported on TiO2 Nanotubes

C,N ‐modified TiO 2 ‐supported Mn–Ce–Co x ‐based catalyst for low‐temperature NH 3 ‐SCR

Advanced Mnox/Tio2 Catalyst with Preferentially Exposed Anatase {001} Facet for Low-Temperature Scr of No

Mechanistic Investigation of the Enhanced SO2 Resistance of Co-modified MnOx Catalyst for the Selective Catalytic Reduction of NOx by NH3

Flexible Ti Mesh-Supported MnO x –CuO x /TiO 2 Nanosheet Monolithic Catalysts for Low-Temperature Selective Catalytic Reduction of NO x with NH 3

CuOx and WOx modified CeO2-TiO2 with various morphologies for the selective catalytic reduction of NOx with NH3

Design of robust Co-doped Mn3O4 spinel catalysts for selective catalytic reduction of NO with NH3 at low temperatures

Novel Homogeneous and Mesoporous MnOx-Doped Ceria Nanosheets As Catalysts for Low-Temperature Selective Catalytic Reduction

Tuning the Property of Mn-Ce Composite Oxides by Titanate Nanotubes to Improve the Activity, Selectivity and SO2/H2O Tolerance in Middle Temperature NH3-SCR Reaction

VxMn(4-x)Mo3Ce3/Ti catalysts for selective catalytic reduction of NO by NH3

Unusual positive effect of SO2 on Mn-Ce mixed-oxide catalyst for the SCR reaction of NOx with NH3

Manganese Oxide Catalysts Supported on Zinc Oxide Nanorod Arrays: A New Composite for Selective Catalytic Reduction of NOx with NH3 at Low Temperature

Probing the role of nanoconfinement in improving N 2 selectivity of Mn-based catalysts during NH 3 -SCR