Abstract:One‐dimensional structured γ‐MnOOH nanorods were prepared by a simple and easy hydrothermal method, and the growth mechanism of γ‐MnOOH nanorods in the hydrothermal reaction system was proposed and discussed. The electrochemical test results show that the γ‐MnOOH nanorods exhibit high charge storage capacity as well as excellent cycle life. MnOOH has received much attention from researchers as a supercapacitor electrode material. In this article, one‐dimensional γ‐MnOOH nanorods were prepared by the hydrothermal method using the redox reaction between MnO4− and Mn2+, and the effects of temperatures on the crystalline phases and electrochemical properties of the samples were investigated. The materials were characterized using XRD, FT‐IR, SEM, TEM, Raman and XPS; electrochemical properties were tested using CV, GCD and EIS. The results show that the reaction temperature plays an important role in the generation of γ‐MnOOH. The samples were pure phases of γ‐MnOOH (M‐140) at the reaction temperature of 140 °C, showing interlaced nanorod morphology, and when the reaction temperature was increased to 180 °C, a mixed phase of MnOOH and Mn3O4 appeared. In contrast, the electrochemical performance of γ‐MnOOH nanorods (M‐140) was superior to the other samples, reaching a specific capacitance of 221 F/g at a current density of 0.2 A/g. The capacitance retention was 93.8 % after charging and discharging the M‐140 2000 times at a current density of 6 A/g. Supercapacitors assembled with γ‐MnOOHand activated carbon (AC) have excellent energy storage performance, and a high energy density of 40.6 Wh/kg is obtained at a power density of 196.7 W/kg.

Hydrothermally synthesised α-MnO2 and β-MnO2 nanorods for pseudocapacitor electrode applications

High Pseudocapacitive Performance of MnO2 Nanowires on Recyclable Electrodes

Synthesis of MnO2/N-doped Ultramicroporous Carbon Nanospheres for High-Performance Supercapacitor Electrodes

Al-doped α-MnO 2 for high mass-loading pseudocapacitor with excellent cycling stability

Rational Design of 2D Manganese Phosphate Hydrate Nanosheets as Pseudocapacitive Electrodes

Enhanced pseudocapacitance from finely ordered pristine alpha-MnO2 nanorods at favourably high current density using redox additive

Hydrothermal Synthesis and Pseudocapacitance Properties of Mno2 Nanostructures

Different Phase and Morphology Effect of Manganese Oxide on Electrochemical Performance for Supercapacitor Application

Synthesis and Electrochemical Properties of One‐Dimensional γ‐MnOOH Nanorods

Enhanced Pseudocapacitive Performance of Α-Mno2 by Cation Preinsertion.

Preparation and electrochemical performance of MnO2 nanorods as electrode materials for supercapacitor

Morphology-controlled synthesis of one-dimensional zinc molybdate nanorods for high-performance pseudocapacitor electrode application

Nanostructured MnO2: Hydrothermal Synthesis and Electrochemical Properties As a Supercapacitor Electrode Material

Nanostructured Manganese Dioxide for Hybrid Supercapacitor Electrodes

Synthesis of δ-MnO2 with nanoflower-like architecture by a microwave-assisted hydrothermal method

beta phase manganese dioxide nanorods Synthesis and characterization for supercapacitor applications

Enhanced Supercapacitor and Cycle-Life Performance: Self-Supported Nanohybrid Electrodes of Hydrothermally Grown MnO2 Nanorods on Carbon Nanotubes in Neutral Electrolyte

Manganese Oxide-Enriched Copper Oxide (Mn2O3/CuO) Nanocomposite Electrodes for Supercapacitor Application

Co‐MnO 2 Nanorods for High‐Performance Sodium/Potassium‐Ion Batteries and Highly Conductive Gel‐Type Supercapacitors

Investigating the Influence of Sodium Preintercalation on the Electrochemical Behavior of Ultrathin MnO 2 Nanowires for Enhanced Supercapacitor Performance

Ni/Mn electroactive nanohybrids physic-chemical properties for ulterior new generation of supercapacitors