Abstract:One‐dimensional structured γ‐MnOOH nanorods were prepared by a simple and easy hydrothermal method, and the growth mechanism of γ‐MnOOH nanorods in the hydrothermal reaction system was proposed and discussed. The electrochemical test results show that the γ‐MnOOH nanorods exhibit high charge storage capacity as well as excellent cycle life. MnOOH has received much attention from researchers as a supercapacitor electrode material. In this article, one‐dimensional γ‐MnOOH nanorods were prepared by the hydrothermal method using the redox reaction between MnO4− and Mn2+, and the effects of temperatures on the crystalline phases and electrochemical properties of the samples were investigated. The materials were characterized using XRD, FT‐IR, SEM, TEM, Raman and XPS; electrochemical properties were tested using CV, GCD and EIS. The results show that the reaction temperature plays an important role in the generation of γ‐MnOOH. The samples were pure phases of γ‐MnOOH (M‐140) at the reaction temperature of 140 °C, showing interlaced nanorod morphology, and when the reaction temperature was increased to 180 °C, a mixed phase of MnOOH and Mn3O4 appeared. In contrast, the electrochemical performance of γ‐MnOOH nanorods (M‐140) was superior to the other samples, reaching a specific capacitance of 221 F/g at a current density of 0.2 A/g. The capacitance retention was 93.8 % after charging and discharging the M‐140 2000 times at a current density of 6 A/g. Supercapacitors assembled with γ‐MnOOHand activated carbon (AC) have excellent energy storage performance, and a high energy density of 40.6 Wh/kg is obtained at a power density of 196.7 W/kg.

beta phase manganese dioxide nanorods Synthesis and characterization for supercapacitor applications

Fabrication and Electrochemical Performance of Nanofibrous Micro-Frameworks of Α-Mno2

Preparation and electrochemical performance of MnO2 nanorods as electrode materials for supercapacitor

Preparation and electrochemical performances of α-MnO2 nanorod for supercapacitor

Synthesis of MnO2/N-doped Ultramicroporous Carbon Nanospheres for High-Performance Supercapacitor Electrodes

Synthesis and Electrochemical Properties of One‐Dimensional γ‐MnOOH Nanorods

Manganese Oxide-Based Electrode Behavior As Materials for Electrochemical Supercapacitors

Green synthesis of MnO x nanostructures and studies of their supercapacitor performance

Hydrothermally synthesised α-MnO2 and β-MnO2 nanorods for pseudocapacitor electrode applications

A simple facile synthesis for phase transforming of δ-MnO2 into α-MnO2 and thereby enhancing Na-ion supercapacitive performance

Nanostructured MnO2: Hydrothermal Synthesis and Electrochemical Properties As a Supercapacitor Electrode Material

Morphological and Electrochemical Cycling Effects in MnO2 Nanostructures by 3D Electron Tomography

A novel method to prepare nanostructured manganese dioxide and its electrochemical properties as a supercapacitor electrode

Different Phase and Morphology Effect of Manganese Oxide on Electrochemical Performance for Supercapacitor Application

Synthesis and Kinetic Analysis of «-MnO2 Nanowires for Supercapacitor Electrode

The Fabrication of Mno2 Nanoparticle for Supercapacitor Application

Synthesis and characterization of α-MnO2 nanoneedles for electrochemical supercapacitors

Synthesis and Characterization of Manganese dioxide Agglomerated Nanoparticles for Supercapacitor Application

Facile Synthesis and Characterization of MnO2 Nanomaterials As Supercapacitor Electrode Materials

Nanostructured Manganese Oxides and Their Composites with Carbon Nanotubes As Electrode Materials for Energy Storage Devices

Manganous-Manganic Oxide@Carbon Core-Shell Nanorods for Supercapacitors with High Cycle Retention