Abstract:One‐dimensional structured γ‐MnOOH nanorods were prepared by a simple and easy hydrothermal method, and the growth mechanism of γ‐MnOOH nanorods in the hydrothermal reaction system was proposed and discussed. The electrochemical test results show that the γ‐MnOOH nanorods exhibit high charge storage capacity as well as excellent cycle life. MnOOH has received much attention from researchers as a supercapacitor electrode material. In this article, one‐dimensional γ‐MnOOH nanorods were prepared by the hydrothermal method using the redox reaction between MnO4− and Mn2+, and the effects of temperatures on the crystalline phases and electrochemical properties of the samples were investigated. The materials were characterized using XRD, FT‐IR, SEM, TEM, Raman and XPS; electrochemical properties were tested using CV, GCD and EIS. The results show that the reaction temperature plays an important role in the generation of γ‐MnOOH. The samples were pure phases of γ‐MnOOH (M‐140) at the reaction temperature of 140 °C, showing interlaced nanorod morphology, and when the reaction temperature was increased to 180 °C, a mixed phase of MnOOH and Mn3O4 appeared. In contrast, the electrochemical performance of γ‐MnOOH nanorods (M‐140) was superior to the other samples, reaching a specific capacitance of 221 F/g at a current density of 0.2 A/g. The capacitance retention was 93.8 % after charging and discharging the M‐140 2000 times at a current density of 6 A/g. Supercapacitors assembled with γ‐MnOOHand activated carbon (AC) have excellent energy storage performance, and a high energy density of 40.6 Wh/kg is obtained at a power density of 196.7 W/kg.

Facile Synthesis and Characterization of MnO2 Nanomaterials As Supercapacitor Electrode Materials

Low-temperature Synthesis of Na2Mn5O10 for Supercapacitor Applications

Nanostructured MnO2: Hydrothermal Synthesis and Electrochemical Properties As a Supercapacitor Electrode Material

Manganese Oxide-Based Electrode Behavior As Materials for Electrochemical Supercapacitors

Facile Fabrication of Mesoporous Manganese Oxides As Advanced Electrode Materials for Supercapacitors

Synthesis and Kinetic Analysis of «-MnO2 Nanowires for Supercapacitor Electrode

Synthesis of MnO2/N-doped Ultramicroporous Carbon Nanospheres for High-Performance Supercapacitor Electrodes

Facile Synthesis of Tremella-Like MnO2 and Its Application As Supercapacitor Electrodes

The Preparation of Nanostructure MnO_2 for Supercapacitor Electrode Material by Electrodeposition

Molten Salt Synthesis of Na‐Mn‐O Composites As Electrode Materials for High‐Performance Supercapacitors

Preparation and electrochemical performance of MnO2 nanorods as electrode materials for supercapacitor

Influence of iron concentration and post-annealing temperature on structure and pseudocapacitive characteristics of a MnO2–Fe2O3 nanocomposite

Synthesis and Electrochemical Properties of One‐Dimensional γ‐MnOOH Nanorods

Preparation and electrochemical performances of α-MnO2 nanorod for supercapacitor

Synthesis and Characterization of Manganese dioxide Agglomerated Nanoparticles for Supercapacitor Application

Facile Synthesis of Ultrafine and Highly Dispersible MnO2 Nanoparticles for Energy Storage in Supercapacitors

Synthesis and capacitance performances of Ni–Mn-Oxides as electrode materials for high-performance supercapacitors

Syntheses and Charge-Discharge Properties of Crystallite Na0.7MnO2.05 in Water Solutions

Synthesis of δ-MnO2 with nanoflower-like architecture by a microwave-assisted hydrothermal method

Synthesis and Characterization of Nickel-doped Manganese Dioxide Electrode Materials for Supercapacitors

Green synthesis of MnO x nanostructures and studies of their supercapacitor performance