Abstract:The caking and adhesion of intermediate product on reactor surfaces during TiO2 production via the NaOH molten salt method are a serious problem. The consolidation of intermediate product can lead to low heat transfer efficiency and low titanium fractional conversion. Furthermore, frequent cleaning is generally required. An anti-caking method that can be applied during low-grade titanium slag decomposition in the NaOH system was studied. The method, which involves the two-step reaction of low-grade titanium slag with molten NaOH without the introduction of additives, can significantly reduce the extent of caking. The NaOH and low-grade titanium slag mixture was first reacted at 350°C for 60min. The temperature was then increased to 550°C in 40min. Finally, the mixture was reacted at 550°C for 75min. The effects of the reaction temperatures, NaOH-to-slag mass ratio and the reaction time on the titanium extraction were investigated. The Brunauer–Emmett–Teller (BET) surface area and apparent density were used to characterize the extent of caking. In the low grade titanium slag, silicate phase prior to pseudobrookite phase reacts with molten NaOH at 350°C in the process of two-step molten reaction and formed sodium silicate. Microstructural and Fourier transform infrared (FT-IR) absorption results show that the firstly formed sodium silicate did not diffuse into the entire reaction system and powder-shaped intermediate product was formed. Approximately 97% of titanium in the titanium slag could be extracted under the optimal reaction conditions. In addition, the content of TiO2 obtained in the product reached 99.3%.

Microwave-assisted preparation of nanocluster rutile TiO2 from titanium slag by NaOH-KOH mixture activation

Preparation of rutile titanium dioxide pigment from low-grade titanium slag pretreated by the NaOH molten salt method

Study of the oxygen reduction of low valent titanium in high titanium slag by microwave rapid heating

Preparation of synthetic rutile from high titanium slag using microwave heating

Multi-scale investigation of the formation and properties of high-grade rutile TiO2 from titanium slags using microwave heating

Evaluation of the structure and valence state of titanium oxide in titania slag under microwave heating

Novel Process for Titanium Dioxide Production from Titanium Slag: NaOH-KOH Binary Molten Salt Roasting and Water Leaching

A novel preparation of titanium dioxide from titanium slag

Preparation and Photocatalytic Activities of TiO2 Nanotubes with Mixed Crystal Structure

Anti-caking in the production of titanium dioxide using low-grade titanium slag via the NaOH molten salt method

Simultaneous removal of Cr(III) and V(V) and enhanced synthesis of high-grade rutile TiO2 based on sodium carbonate decomposition

Phase transition kinetics and strengthening mechanism of rutile TiO2 prepared by microwave-enhanced calcination of TiC-doped metatitanic acid

RAPID SYNTHESIS OF NANO-TITANIUM DIOXIDE BY COMBUSTION METHOD AND ITS PHOTO-CATALYSIS PERFORMANCE

Mechanochemical activation of titanium slag for effective selective catalytic reduction of nitric oxide

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

Study on Preparation of Metatitanic Acid by Hydrolysis in the Process of Producing Titanium Dioxide by Decomposition of Titanium Slag with Alkali Molten Salt

Highly efficient oxidation of Panzhihua titanium slag for manufacturing welding grade rutile titanium dioxide

Treatment of nano-sized rutile phase TiO2 powder under ultrasonic irradiation in hydrogen peroxide solution and investigation of its sonocatalytic activity.

Ordered Mesoporous Thin Films Of Rutile Tio2 Nanocrystals Mixed With Amorphous Ta2o5

A process for producing synthetic rutile from Panzhihua titanium slag