Assemble a new functional PEDOT-ZIS electrode for sustainable and efficient treatment of wastewater in photoelectrocatalytic system

Bo Gao,Yupeng Wang,Miao Zhang,Jiadong Liu,Lei Wang,Fawzi Banat,Mika Sillanpää
DOI: https://doi.org/10.1016/j.jwpe.2020.101513
IF: 7
2020-10-01
Journal of Water Process Engineering
Abstract:<p>Poly (3,4-ethylenedioxythiophene) (PEDOT), which served as photosensitizer and holes transport agent, was polymerized on ternary Zn-In-S film (ZIS) for enhanced photoelectrocatalytic (PEC) activity. The photogenerated electrons and holes can be effectively separated, which can enhance photoelectrocatalytic activity on methylene blue (MB) degradation. The MB decolorization and mineralization rate can reach 96 % and 53 % under the optimal degradation condition with applied voltage of -0.3 V and pH 4 under reaction time of 180 min. In addition, the PEDOT-ZIS composite electrode exhibited good stability after 5 consecutive cycles of experiments. Hydroxyl radical (·OH), superoxide radical (·O<sub>2</sub><sup>−</sup>) and singlet oxygen (<sup>1</sup>O<sub>2</sub>) were detected in the PEC system using PEDOT-ZIS as electrode. 2.37 × 10<sup>-2</sup> mmol·l<sup>-1</sup> of <sup>1</sup>O<sub>2</sub> was generated by PEDOT-ZIS composite electrode through photosensitization of PEDOT coating layer. Also 1.70 × 10<sup>-2</sup> mmol·l<sup>-1</sup>·O<sub>2</sub>- was produced through oxygen reduction by photogenerated electrons. In comparison, no <sup>1</sup>O<sub>2</sub> was detected in pure ZIS electrode system. More negative conduction band was obtained for PEDOT-ZIS composite electrode, which was more conducive to the generation of reactive radicals through electron reduction. Electrochemical impedance spectroscopy and photoluminescence spectra measurements reflected lower charge transfer resistance and recombination of electron-hole pairs in PEDOT-ZIS system.</p>
engineering, chemical, environmental,water resources
What problem does this paper attempt to address?
The main problem that this paper attempts to solve is to improve the efficiency and sustainability of the photoelectrocatalytic system in wastewater treatment. Specifically, the author prepared a new type of functional PEDOT - ZIS electrode by polymerizing poly(3,4 - ethylenedioxythiophene) (PEDOT) on the ternary Zn - In - S (ZIS) thin film to enhance the photoelectrocatalytic activity. The goal of the research is to increase the degradation rate of methylene blue (MB) through this modified electrode, thereby achieving more efficient and sustainable wastewater treatment. ### Main problem analysis: 1. **Effective separation of photogenerated electrons and holes**: - The research found that by polymerizing PEDOT on the ZIS thin film, the photogenerated electrons and holes can be effectively separated, thereby enhancing the photoelectrocatalytic activity. This helps to reduce the recombination of electrons and holes and improve the quantum efficiency of the system. 2. **Increasing the degradation rate of methylene blue**: - The experimental results show that under the optimal conditions (applied voltage - 0.3 V, pH 4, reaction time 180 minutes), the decolorization rate and mineralization rate of MB reached 96% and 53% respectively. This indicates that the PEDOT - ZIS composite electrode has significant advantages in the photoelectrocatalytic degradation of MB. 3. **Stability and reusability of the electrode**: - The research also tested the stability of the PEDOT - ZIS composite electrode. After 5 consecutive experiments, the electrode still showed good performance, indicating that it has good stability and reusability. 4. **Discussion of the reaction mechanism**: - By detecting free radicals (such as hydroxyl radical (·OH), superoxide radical (·O₂⁻) and singlet oxygen (¹O₂)), the research revealed the generation mechanism of active species in the photoelectrocatalytic system. For example, the PEDOT - ZIS composite electrode produced 2.37 × 10⁻² mmol·L⁻¹ of ¹O₂ and 1.70 × 10⁻² mmol·L⁻¹ of ·O₂⁻ under illumination, and these active species played a key role in the degradation of MB. ### Conclusion: This paper successfully solved the problem of rapid recombination of photogenerated electrons and holes in the photoelectrocatalytic system by preparing the PEDOT - ZIS composite electrode, increased the degradation rate of methylene blue, and verified the stability and reusability of the electrode. These results provide an important theoretical and experimental basis for the development of efficient photoelectrocatalytic wastewater treatment technologies.