Fabrication of Er:SrF2 transparent ceramics by air pre-sintering and hot isostatic pressing

Yagang Feng,Guimin Chen,Lihao Guo,Xinyou Huang,Ziyu Liu,Feng Tian,Tengfei Xie,Zhengfa Dai,Dariusz Hreniak,Jiang Li

DOI: https://doi.org/10.1016/j.optmat.2023.114009

IF: 3.754

2023-08-01

Optical Materials

Abstract:Using the 1 at.% Er:SrF2 nano-powders synthesized by the co-precipitation method as starting powders, 1 at.% Er:SrF2 transparent ceramics were successfully prepared by air pre-sintering at different temperatures for 2 h combined with hot isostatic pressing (HIP) post-treatment at 600 °C for 2 h under 100 MPa Ar. The influences of the pre-sintering temperature on optical quality, microstructure, phase composition and EPR spectrum of ceramics were investigated. Among all the HIP post-treated 1 at.% Er:SrF2 ceramics in the thickness of 2.5 mm, the sample pre-sintered at 650 °C shows the best optical quality, whose transmittance at 2500 nm and 1500 nm reaches 83.4% and 73.6%, respectively. Furthermore, the spectral characteristics of this ceramic sample were systematically analyzed. The fluorescence lifetime for the 1 at.% Er:SrF2 ceramics at 1530 nm is 49.62 ms. The strongest absorption and emission cross section for the peaks at around 1530 nm are 6.20 × 10−21 and 3.47 × 10−21 cm2, respectively. In brief, the above findings indicate that the Er:SrF2 ceramics is a promising candidate as middle infra-red laser gain media.

materials science, multidisciplinary,optics