Abstract:Fluoride-upconversion transparent ceramic materials doped with Er ions have attracted extensive interest due to their higher stability, lower phonon energy, and higher upconversion efficiency. xEr:Sr5(PO4)3F (S-FAP) (x=0.5–5 at%) transparent ceramics have been synthesized by hot pressing sintering in this work, and the maximum optical transmittance of the sample reached 74.52 and 82.45% at 500 and 1000 nm, respectively. The XRD results of the powder and ceramic samples were consistent with the diffraction characteristics of the hexagonal S-FAP crystal structure. The SEM and TEM images of powder revealed that the morphology of the sample was composed of mostly rice grains with a diameter of around 20 nm. The XPS and EDS results confirmed the presence of Er3+ and the uniform distribution of Er elements. The thermally etched surface and cross section of ceramics revealed residual pores as the most important scattering source, and the SEM images of the ceramics show that Er doping can obviously promote the growth of the average grain size of S-FAP transparent ceramics. Furthermore, the upconversion luminescence characteristics and fluorescence lifespan of S-FAP transparent ceramics with varied Er doping concentrations were examined, as well as the upconversion luminescence process. The findings in this work indicate that Er:S-FAP transparent ceramics can be employed as a potential upconversion fluorescent material in display technology, biomedicine, temperature sensing, and other applications.

Fabrication and spectral properties of Dy: SrF2 transparent ceramics

Fabrication and optical characterizations of PrF3-doped SrF2 transparent ceramics

Fabrication and spectroscopic investigations on Er3+, Ho3+: SrF2 transparent ceramics for 2.7 μm emission

Preparation and Luminescence Properties of Ce3+/Dy3+-codoped Fluorosilicate Glass Ceramics

Effect of Cr3+ Doping Concentration on the Microstructure, Mechanical Properties and Optical Properties of Cr3+: SrF2 Transparent Ceramics

Microstructure and Luminescence of Yb3+-doped Fluorosilicate Glass Ceramics

Fabrication, microstructure and laser performance of Yb3+ doped CaF2-YF3 transparent ceramics

The Preparation and Photoluminescence Properties of Fluorosilicate Glass Ceramics Containing CeF3:Dy3+ Nanocrystals

Fabrication, microstructure and upconversion luminescence properties of Er:Sr5(PO4)3F transparent nanostructured ceramics

Improving Multifunctional Performance of Dy-doped (ba0.85ca0.15)(zr0.1ti0.9)o< Sub>3 Ceramics Via Tailoring Dy-doping Amount and Ceramic Processing

Fabrication and spectroscopic properties of hot-pressed Tb:CaF2 transparent ceramics with different doping concentrations

Energy transfer and controllable colors of upconversion emission in Er3+ and Dy3+ co-doped CaF2 transparent ceramics

Energy transfer and color tunable up-conversion luminescence in PrF3 and YbF3 co-doped SrF2 transparent ceramics

Fabrication and optical characterizations of hot-pressed transparent SrF2/Nd:SrF2/SrF2 composite ceramic

Densification and microstructure evolution of hot-pressed Er:SrF2 transparent ceramics

Microstructural, spectroscopic and mechanical properties of hot-pressed Er:SrF2 transparent ceramics

Fabrication and upconversion luminescence properties of Er:SrF2 transparent ceramics compared with Er:CaF2

The Preparation and Photoluminescence Properties of Fluorosilicate Glass Ceramics Containing CeF <sub>3</sub> :Dy <sup>3+</sup> Nanocrystals

CRYSTALLIZATION BEHAVIOR AND WHITE LIGHT EMISSION PROPERTY OF Tm~(3+) AND Dy~(3+) CO-DOPED OXYFLUORIDE ALUMINOBOROSILICATE GLASSES

Transparent hexagonal Yb:Sr5(PO4)3F ceramics fabricated by hot pressing sintering with LiF doping

Tailoring Multifunctional Performance of Dy-doped (ba0.85ca0.15)(zr0.1ti0.9)o3 Ceramics Via Optimizing Ceramic Processing