Alkali Metal Ion-Regulated Lead-free, All-Inorganic Double Perovskites for HTM-free, Carbon-Based Solar Cells
Jiabao Li,Jialong Duan,Jian Du,Xiya Yang,Yudi Wang,Peizhi Yang,Yanyan Duan,Qunwei Tang
DOI: https://doi.org/10.1021/acsami.0c11770
2020-09-28
Abstract:Quaternary Cs<sub>2</sub>AgBiBr<sub>6</sub> perovskites have been considered as a potential candidate to simultaneously resolve the lead toxicity and instability issues of unprecedented organic–inorganic hybrid halide perovskites. Unfortunately, the photovoltaic efficiency is still lower owing to the great challenge to make high-quality Cs<sub>2</sub>AgBiBr<sub>6</sub> film with fewer defects. Herein, we demonstrate alkali metal ions including Li<sup>+</sup>, Na<sup>+</sup>, K<sup>+</sup>, and Rb<sup>+</sup> as mediators to regulate the crystal lattice and film quality of Cs<sub>2</sub>AgBiBr<sub>6</sub> perovskites. A less-pinhole perovskite film is obtained by precisely controlling the doping dosage and element species, significantly reducing the defects. When assembled into a hole-transporting material-free, carbon-electrode perovskite solar cell, a significantly enhanced efficiency of 2.57% compared to the undoped device with 1.77% efficiency has been achieved owing to the suppressed shunt current loss. Additionally, this device displays superior tolerance under high-temperature and air conditions without encapsulation, providing new opportunities to promote the future development of lead-free Cs<sub>2</sub>AgBiBr<sub>6</sub> perovskites in the photoelectric field.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c11770?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c11770</a>.Experimental details, element mapping images, XPS spectra, 3D AFM images, contact angles, electron mobility, UV–vis absorbance spectra and UPS spectra of Cs<sub>2</sub>AgBiBr<sub>6</sub> films; <i>J</i>–<i>V</i> curves; XRD patterns of Li<sup>+</sup>-doped perovskite films; cross-sectional SEM images of PSCs; <i>J</i>–<i>V</i> curves of hole-only devices; and <i>V</i><sub>oc</sub> decay curves of various PSCs (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c11770/suppl_file/am0c11770_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology