The effect of Y and Nd additions on the microstructure and creep behavior of AZ80

Lingbao Ren,Carl J. Boehlert,Gaofeng Quan
DOI: https://doi.org/10.1016/j.msea.2020.140397
2021-01-01
Abstract:<p>The effect of yttrium (0.2Y wt.%) and yttrium + neodyminum (0.1Y+0.1Nd wt.%) additions on the long-term (&gt;1200 h) tensile creep and microstructural evolution of AZ80 were investigated at temperatures ranging between 100 °C and 150 °C and stresses ranging between 50 MPa and 100 MPa. The alloying resulted in both the formation of Y- and/or Nd containing particles, and lower tensile strengths and elongation-to-failure. The minimum creep rate (<span class="math"><math>ε˙min</math></span>) increased with increasing applied creep temperature and stress. Y addition resulted in greater creep-resistance compared with that for (Y + Nd) additions. The <span class="math"><math>ε˙min</math></span> of AZ80 + 0.2Y was approximately half that of AZ80 at 50 MPa at 150 °C. The apparent-creep-activation-energy for each alloy ranged between 73 and 93 kJ/mol, and pipe-diffusion-assisted dislocation creep was suggested to be the dominant secondary stage creep deformation mechanism. Discontinuous precipitation (DP) occurred in AZ80 during the creep exposure but was impeded by precipitate-containing twins. The DP was less concentrated in the Y and (Y + Nd) containing alloys, which exhibited lower Vickers hardness values than AZ80. Grain boundary and twin boundary cavitation/cracking were prevalent during creep. Minor Y or (Y + Nd) addition resulted in less oxidation of AZ80 and extended the intermediate-temperature creep life.</p>
materials science, multidisciplinary,nanoscience & nanotechnology,metallurgy & metallurgical engineering
What problem does this paper attempt to address?