Dressing of Diamond Grinding Wheels with Abrasive Water Jet for RB-SiC Surface Grinding
Zhenzhong Zhang,Chong Wang,Peng Yao,Jun Wang,Chuanzhen Huang,Ke Zhang,Yue Liu
2018-01-01
Abstract:To realize the high efficiency and precision machining of reaction sintered silicon carbide (RB-SiC). An on-machine abrasive waterjet method is proposed for dressing a metal-bonded diamond grinding wheel in this paper. These wheels were used for grinding RB-SiC. The grinding force and surface roughness were measured during the grinding process. The influence of grinding process parameters on the surface grinding force and surface roughness of the workpiece were analyzed by orthogonal experiments. This study provides an applicable method for controlling the surface quality of precision ground RB-SiC with the metal bonded diamond grinding wheel. Introduction High precision, ultra-smooth and lightweight primary mirror is the key to a new generation of space camera and other large high resolution optical remote sensing system[1]. Reaction sintered silicon carbide is expected to be one of the most excellent materials for space optics due to their many superior properties, such as high stiffness, high thermal conductivity, high wear resistance, and low thermal expansion coefficient. However, as a typical hard and brittle materials, reaction-bonded silicon carbide (RB-SiC) is difficult to achieve a high efficiency and low damage ultra-precision machining, which limits their further application in optical fields[2,3]. Precision grinding with a diamond wheel is regarded as one of the most appropriate methods to machine these hard and brittle materials[4], which is often used to reduce the shape errors rapidly in rough machining of a large-aperture aspheric mirror. However, the resinoid bonded diamond wheel wear is inevitable and fast during the machining process, which not only affect the surface roughness but also the form accuracy of the workpiece. Compared with resin bonded diamond grinding wheel, metal bonded diamond grinding wheel is easier to ensure the machining accuracy due to its higher strength, hardness, and lower wear rate. However, the form accuracy, surface and subsurface quality of the mirror will degrade seriously if the metal bonded grinding wheel is not timely dressed because of its poor self-sharpening [5]. Moreover, it is difficult to dress the metal bonded grinding wheel with the traditional mechanical dressing method. Potential problems still need to be solved in conventional dressing, such as wear of the dressing tool and low dressing efficiency[6]. To address these problems, the abrasive waterjet technology was performed for dressing the wheel. Compared with conventional dressing methods, abrasive waterjet dressing neither causes mechanical damage on grains nor does it leads to a thermal effect on the grinding wheel. Thus, it is a promising tool for dressing of the wheel by abrasive waterjet[7]. Many efforts have been made by previous researchers in abrasive waterjet dressing. Hirao et al. [8] offered a proposal of using high-pressure waterjet to remove chips from the metal bonded CBN wheel without damaging the wheel. Axinte et al. [9] reported on a specific application of AWJ turning, i.e. truing and dressing of Al2O3 grinding wheels. The results of the experiment demonstrated that abrasive waterjet turning integrates the kinematics of a conventional turning process with the advantages of abrasive waterjet cutting. It will remove abrasive grits as well as binder on the circumference of the grinding wheel progressively. The results also showed that the accuracy of the trued wheel profile decreases as the stand-off distance increasing. Yao et al. [10] investigated the effect of AWJ dressing of resinoid bonded diamond wheels and concluded that the dressing effect of abrasive waterjet is superior to pure waterjet. The protrusion height of the diamond grits becomes distinct and the abrasive grains distribute uniformly on the wheel surface after dressing with abrasive waterjet. Although the abrasive waterjet dressing has been widely investigated, a limited number of studies which focused on the on-machine dressing metal bonded diamond wheel during grinding of RB-SiC have been reported. In this study, the abrasive waterjet technology for dressing the metal bonded grinding wheel is introduced. The wheel surface topography before and after abrasive water jet dressing was compared and analyzed. In order to find the influence of the grinding parameters such as wheel speed, cutting depth, crossfeed rate and axial feed on the surface roughness and grinding force, the experiments of grinding of RB-SiC using the AWJ dressed diamond wheel were conducted by an orthogonal test method. Experimental setup and Procedure The experiments were conducted on an ultra-precision surface grinding machine NAS520 CNC. In these experiments, an on-machine dressing process termed abrasive waterjet dressing was used. The dressing process is illustrated in Fig. 1, and the detail dressing parameters are listed in Table 1. The metal bonded wheel size is about 200 mm in diameter and 8 mm in depth. The average grit size is 120 mesh. The topographies of wheel surface before and after dressing were observed by a 3D laser scanning confocal microscope (Keyence VK-X200K). The RB-SiC ceramics employed in the experiments is fabricated by Changchun Institute of Optics, Fine Mechanics and Physics, CAS. The material properties of the samples are shown in Table 2. The workpiece was clamped on the three-component force dynamometer and fixed on the table of the surface grinder. The average surface roughness (Ra) of the workpiece was measured at five different positions on the surface by a portable surface roughness tester. The measuring direction is vertical to the feed direction of the table. In order to find the influence of the grinding parameters (including wheel speed, cutting depth, cross feed rate and axial feed) on the surface roughness and grinding force, the grinding experiments were conducted in this paper by an orthogonal test method. The orthogonal test method is a kind of designing method to study many factors and levels. It conducts tests by selecting a suitable number of representative test cases from many test data, which have evenly dispersed, neat comparable characteristics. The design of orthogonal experimental is based on the orthogonal table. Table 3 lists the factors and levels of the orthogonal experiment in which four grinding parameters including (A) wheel speed (B) cutting depth, (C) feed rate, and (D) axial feed were selected. Each parameter has five levels to be optimized. Twenty-five trials were carried out according to the L25 (5 ) array to grinding RB-SiC to complete the optimization process. Table 1 The detail dressing parameters Orifice diameter (mm) 0.25 Nozzle diameter (mm) 0.76 Abrasive in waterjet 150# (75 to 106 μm) Jet pressure(MPa) 40 Standoff distance(mm) 20 Wheel speed(m/s) 5 Table 2 Physical and mechanical properties of RB-SiC ceramics Property Values Density (g/cm) 3.0 Young modulus (GPa) 350 Poisson's ratio υ 0.24 Thermal conductivity (W/m×k) 144[11] Thermal expansion coefficient (K×10) 2.4 Table 3 The factors and levels of the orthogonal experiment