Improving plasticity by Si-addition-induced coherent nanoprecipitates in Cu-Al-Mn alloy fabricated by laser powder bed fusion

Ying Li,Mingzhu Dang,Honghao Xiang,Yue Hou,Qingsong Wei
DOI: https://doi.org/10.1016/j.jmrt.2024.09.035
IF: 6.267
2024-09-13
Journal of Materials Research and Technology
Abstract:In this paper, the Cu-10.8Al-8.3Mn-0.37Si alloy containing Mn 5 Si 3 phase was obtained by adding Si element to the Cu-10.8Al-8.3Mn alloy. The two alloys were printed by laser powder bed fusion. The changes in the organization and tensile properties of the alloys and the mechanism were investigated. After Si addition, the Mn 5 Si 3 nano phase precipitated in the alloy in addition to the β 1 austenite phase. The Mn 5 Si 3 phase was co-lattice with the β 1 phase with an average size of 10 nm and was diffusely distributed. Standard tensile experiments showed that the yield strength of the Cu-10.8Al-8.3Mn-0.37Si alloy decreased by 57.7% and the elongation increased by 266% compared to the Cu-10.8Al-8.3Mn alloy, while the tensile strength remained essentially unchanged. The presence of Mn 5 Si 3 phase provided nucleation points for martensite and promoted the generation of stress-induced martensite. Hence the yield strength was reduced. TEM results showed that the β 1 phase in the Cu-10.8Al-8.3Mn-0.37Si alloy was fully transformed into stress-induced martensite after deformation, which displayed the transformation induced plasticity effect and hindered the slip of dislocations. Meanwhile, the Mn 5 Si 3 phase was sheared by the stacking faults, which promoted the accumulation of hetero-deformation-induced stress. Therefore, the hardening capacity and plasticity of the Cu-10.8Al-8.3Mn-0.37Si alloy were enhanced. This work provides a new idea for the plasticity enhancement of Cu–Al–Mn-based shape memory alloys achieved by co-lattice nano-precipitated phase strengthening.
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?