Thermo-mechanical behavior of hypoeutectic Ni-Y-Zr alloys

Shruti Sharma,Saurabh Sharma,Samuel Moehring,Jun-Sang Park,Kiran Solanki,Pedro Peralta
DOI: https://doi.org/10.1016/j.mtcomm.2024.108410
IF: 3.8
2024-02-28
Materials Today Communications
Abstract:Microstructure refinement and optimized alloying can improve metallic alloy performance: stable nanocrystalline (NC) alloys with immiscible second phases, e.g., Cu-Ta, are stronger than unstable NC alloys and their coarse-grained (CG) counterparts, but higher melting point matrices are needed. Hypoeutectic, CG Ni-Y-Zr alloys were produced via arc-melting to explore their potential as high-performance materials. Microstructures were studied to determine phases present, local composition and length scales, while heat treatments allowed investigating microstructural stability. Alloys had a stable, hierarchical microstructure with ∼250 nm ultrafine eutectic, ∼10 μm dendritic arm spacing and ∼1 mm grain size. Hardness and uniaxial compression tests revealed that mechanical properties of Ni-0.5Y-1.8Zr (in wt%) were comparable to Inconel 617 despite the small alloying additions, due to its hierarchical microstructure. Uniaxial compression at 600 °C showed that ternary alloys outperformed Ni-Zr and Ni-Y binary alloys in flow stress and hardening rates, which indicates that the Ni 17 Y 2 phase was an effective reinforcement for the eutectic, which supplemented the matrix hardening due to increased solubility of Zr. Results suggest that ternary Ni-Y-Zr alloys hold significant promise for high temperature applications.
materials science, multidisciplinary
What problem does this paper attempt to address?