Abstract:Bimetallic CoCu model catalysts were investigated for the synthesis of higher alcohols using catalytic CO hydrogenation according to the Fischer–Tropsch technology. Emphasis was placed on revealing the influence of the activation conditions. Accordingly, catalyst precursors were activated in argon, hydrogen, syngas (CO/H2), and CO under atmospheric conditions and at elevated temperatures (370 °C). All catalyst precursors were prepared via oxalate coprecipitation in the absence of a classic support. Alcohol selectivities between 30 and ∼40% (up to ∼50% for the sum of alcohols and alkenes) were obtained with an Anderson–Schulz–Flory (ASF) chain lengthening probability maximizing the slate up to C6. Detailed catalysis and characterization studies were performed using a Co2Cu1 catalyst composition. The catalytic performances of the H2- and syngas-activated Co2Cu1 catalyst were similar. While the CO-activated catalyst shows significantly higher catalytic activity and ASF chain lengthening probability, the alcohol selectivities are lower than those of H2- or syngas-activated ones. All catalysts required time on stream for several hours to achieve steady-state catalytic performance. Co2Cu1 catalysts were characterized by temperature-programmed decomposition (TPDec), in situ N2 physisorption (Brunauer–Emmett–Teller), transmission electron microscopy (TEM), and in situ X-ray photoelectron spectroscopy (XPS). The data indicate major restructuring occurs during activation. An “onion-like” graphitic carbon shell was observed via TEM for the CO-activated Co2Cu1 catalyst, which probably originated mainly from the Boudouard reaction (2CO + [ ]ad → Cad + CO2). This interpretation is in accordance with the TPDec profiles and XPS results. The latter also indicates that syngas and CO activation lead to higher than nominal Co/Cu surface ratios. The surface segregation of Co in the presence of CO atmospheres is interpreted on the basis of Co@Cu core–shell structured particles.

Synthesis of n-butanol-rich C3+ alcohols by direct CO2 hydrogenation over a stable Cu–Co tandem catalyst

Accelerating C2+ Alcohols Synthesis from Syngas by Simultaneous Optimizations of CO Dissociation and Chain Growth over CuCo Alloy Catalyst

Realizing and Revealing Complex Isobutyl Alcohol Production over a Simple Cu–ZrO 2 Catalyst

Higher Alcohols through CO Hydrogenation over CoCu Catalysts: Influence of Precursor Activation

Synthesis Of Higher Alcohol Mixtures From Syngas Over Modified Copper Catalysts

Synergy between Active Sites of Ternary CuZnAlOOH Catalysts in CO Hydrogenation to Ethanol and Higher Alcohols

Syngas conversion to higher alcohols via wood-framed Cu/Co-carbon catalyst

Direct Conversion of CO2 into Alcohols Using Cu-Based Zeolite Catalysts

Ni-Based Hydrotalcite (HT)-Derived Cu Catalysts for Catalytic Conversion of Bioethanol to Butanol

Structural evolution of bimetallic Co-Cu catalysts in CO hydrogenation to higher alcohols at high pressure

Direct Conversion of Syngas to Higher Alcohols over Multifunctional Catalyst: The Role of Copper-Based Component and Catalytic Mechanism

The synthesis of higher alcohols from CO2 hydrogenation over Mn-Cu-K modified Fe5C2 and CuZnAlZr tandem catalysts

Optimizing interfacial interaction between Cu and metal oxides boosts methanol yield in CO2 hydrogenation

Ultrastable Cu Catalyst for CO2 Electroreduction to Multicarbon Liquid Fuels by Tuning C–C Coupling with CuTi Subsurface

Fabrication of Highly Stable SiO2 Encapsulated Multiple CuFe Nanoparticles for Higher Alcohols Synthesis via CO Hydrogenation

Design and Synthesis of Spherical-Platelike Ternary Copper-Cobalt-manganese Catalysts for Direct Conversion of Syngas to Ethanol and Higher Alcohols

Concentrated C 2+ Alcohol Production Enabled by Post-Intermediate Modulation and Augmented CO Adsorption in CO Electrolysis

Higher Alcohols Synthesis from Syngas over Cocu/Sio2 Catalysts: Dynamic Structure and the Role of Cu