Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

In situ neutron diffraction study of fatigue behavior of CrFeCoNiMo0.2 high entropy alloy

Investigation of fatigue mesoscopic mechanical properties of a nickel-based superalloy by instrumented microindentation measurements

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Low cycle fatigue performances of Al 0.3 CoCrFeNi high entropy alloys: In situ neutron diffraction studies on the precipitation effects

The Influence of Dwell Time on Low Cycle Fatigue Behavior of Ni-Base Superalloy Ic10

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

In-situ neutron diffraction studies on high-temperature deformation behavior in a CoCrFeMnNi high entropy alloy

A Crystallographic Model for the Orientation Dependence of Low Cyclic Fatigue Property of a Nickel-Base Single Crystal Superalloy

Analysis of Meso-Inhomogeneous Deformation on a Metal Material Surface under Low-Cycle Fatigue

Temperature-dependent fatigue response of a Fe44Mn36Co10Cr10 high entropy alloy: A coupled in-situ electron microscopy study and crystal plasticity simulation

Microstructure sensitivity of the low cycle fatigue crack initiation mechanisms for the Al 0.3 CoCrFeNi high entropy alloy: in-situ SEM study and crystal plasticity simulation

In-situ TOF Neutron Diffraction Studies of Cyclic Softening in Superelasticity of a NiFeGaCo Shape Memory Alloy

Enhancement of fatigue resistance by overload-induced deformation twinning in a CoCrFeMnNi high-entropy alloy

Fatigue-creep Behaviors of Ni–Fe Based Superalloy under Various Testing Conditions

Deformation mechanisms of Mo alloyed FeCoCrNi high entropy alloy: In situ neutron diffraction

Low cycle fatigue behaviors of CrCoNi medium-entropy alloy with different grain sizes

Fatigue Resistance of Nanotwinned High-Entropy Alloy Films

In-situ study of room temperature tensile deformation of a CrMnFeCoNi high-entropy alloy

Investigation of Deformation Inhomogeneity and Low-Cycle Fatigue of a Polycrystalline Material

Deformation mechanisms of CoCrFeMnNi high-entropy alloy under low-cycle-fatigue loading

Microstructure relevant fatigue short crack propagation behavior of Al 0.3 CoCrFeNi high entropy alloy: in-situ SEM study