Effect of annealing temperature in carbon powder on thermoelectric properties of the SrTiO3−δ single crystal in the [111] crystal orientation

Zhixin Ma,Yang Qi,Jun Wang,Xiaoguo Bi,Xu-dong Liu,Xiaodong Li,Ji-guang Li,Xudong Sun

DOI: https://doi.org/10.1016/j.ceramint.2022.03.166

IF: 5.532

2022-03-01

Ceramics International

Abstract:SrTiO3 is a promising thermoelectric material for applications in harsh environments, owing to its excellent thermoelectric (TE) properties and high-temperature stability. The effect of annealing in carbon powders on the TE properties of SrTiO3−δ in the [111] direction was experimentally investigated and analysed using first-principles calculation. The electrical conductivity of the SrTiO3−δ single crystals in the [111] direction increases with an increase in annealing temperature in the range of 1573–1673 K, which is opposite to that in the [510] direction as shown in a previous experiment. This is attributed to the different variation trend of carrier concentration. First-principle calculation results show that the carrier concentration in the [111] direction increases with increasing oxygen vacancy concentration, but it is the opposite in the [510] direction. Strong anisotropy of carrier concentration should be caused by the difference in atomic arrangement, making difference in the amount of free electrons that maybe constrained at high oxygen vacancy in different directions. Although the SrTiO3−δ single crystal annealed at 1573 K shows a lower electrical conductivity, it obtains higher power factor with the maximum value of 2.24 mW m−1 K−2 at 323 K, which is predominantly due to its higher effective mass. It also yields the highest ZT value of 0.18 at 873 K owing to the lower thermal conductivity. The results of this study are imperative for the design and development of perovskite TE materials.

materials science, ceramics