Effect of phase structures and substrate temperatures on NTC characteristics of Cu-modified Ba–Bi–O-based perovskite-type thermistor thin films

Jing-Jing Qu,Sheng Li,Fei Liu,Xiao Liu,Ze-Xing Chen,Chang-Lai Yuan,Xin-Yu Liu,Yun-Yun Zhao,De-Jian Zhou
DOI: https://doi.org/10.1016/j.mssp.2020.105375
IF: 4.1
2021-01-01
Materials Science in Semiconductor Processing
Abstract:<p>Based on the formula of BaBi<sub>0·92</sub>Cu<sub>0·08</sub>O<sub>3</sub>, Cu-modified Ba–Bi–O-based perovskite-like negative temperature coefficient (NTC) thermistor thin films were successfully prepared by radio frequency (RF) magnetron sputtering method with the various deposition temperatures (25 °C, 100 °C, 200 °C and 250 °C). The effects of the substrate temperatures on the phase structures and electrical properties were respectively characterized and investigated by X-ray diffraction (XRD), resistance-temperature measurement, and complex impedance analysis for the Ba–Bi–O-based thin films. Additionally, the cross-sectional microstructures and grain morphologies of the BaBi<sub>0·92</sub>Cu<sub>0·08</sub>O<sub>3</sub> thin films were analyzed by scanning electron microscope (SEM) and atomic force microscope (AFM). The XRD patterns results showed that the perovskite monoclinic structure with a small amount of BaBiO<sub>2.5</sub> s phase could be obtained for the BaBiO<sub>3</sub> thin film deposited at 200 °C, and also, the main crystalline phase was transferred from BaBiO<sub>2.82</sub> to BaBiO<sub>2.5</sub> when the BaBi<sub>0·92</sub>Cu<sub>0·08</sub>O<sub>3</sub> thin films were deposited at 200 °C and 250 °C, respectively. Temperature dependent complex impedance spectroscopy was carried out to make clear the resistance contribution of grain (<em>R</em><sub>g</sub>), grain boundary (<em>R</em><sub>gb</sub>) and contact (<em>R</em><sub>s</sub>) response for the conduction mechanisms in the Ba–Bi–O-based thin film deposited at a given substrate temperature. Compared with the electrical properties of the BaBiO<sub>3</sub> thin film deposited at 200 °C [such as the room-temperature resistivity (<em>ρ</em><sub>25</sub> ~ 1548 Ω cm) and the thermistor constant (<em>B</em><sub>25/85</sub>–3245 K)], the better NTC characteristics of a lower <em>ρ</em><sub>25</sub> value of about 956 Ω cm and a higher <em>B</em> value of approximately 3480 K were found in the BaBi<sub>0·92</sub>Cu<sub>0·08</sub>O<sub>3</sub> thin film deposited at a same temperature (200 °C). It is believed that the phase structures and electrical properties of the BaBiO<sub>3</sub> perovskite-type NTC thermistor thin films could be adjusted and optimized by a trace amounts of Cu-ions substitutions and depositing at an appropriate substrate temperature, which also showed that such as these novel BaBiO<sub>3</sub>-based thin films are feasible with the extensive of actual applications for the NTC thermistors.</p>
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to optimize the negative temperature coefficient (NTC) characteristics of Ba - Bi - O - based perovskite - type NTC thermistor films by studying the effects of copper ion doping and substrate temperature on the phase structure and electrical properties of these films. Specifically, the author hopes to adjust and optimize the phase structure and electrical properties of BaBiO₃ - based perovskite - type NTC thermistor films by changing the deposition temperature and introducing a trace amount of copper ions, in order to obtain a lower room - temperature resistivity (ρ₂₅) and a higher thermosensitive constant (B - value), thereby enhancing their practical application potential as NTC thermistors. ### Research Background NTC thermistor films have received extensive attention due to their fast response speed, high stability, and low operating voltage, especially in fields such as circuit compensation, temperature sensors, surge protection, and solar cells. However, the traditional Mn - Co - Ni - based spinel - structure NTC thermistors have an unstable crystal structure at high temperatures, which limits their practical applications. Therefore, researchers have begun to explore other types of NTC thermistor materials, such as Ba - Bi - O - based perovskite - structure materials, which exhibit excellent NTC characteristics under specific conditions. ### Research Objectives 1. **Optimize Phase Structure and Electrical Properties**: Optimize the phase structure and electrical properties of BaBiO₃ - based perovskite - type NTC thermistor films by changing the deposition temperature and introducing a trace amount of copper ions. 2. **Enhance NTC Characteristics**: Obtain a lower room - temperature resistivity (ρ₂₅) and a higher thermosensitive constant (B - value) to enhance the NTC characteristics of the film materials. 3. **Practical Application Potential**: Verify the feasibility of these optimized film materials in practical applications, especially in the field of NTC thermistors. ### Main Research Methods - **Film Preparation**: Deposit BaBi₀·₉₂Cu₀·₀₈O₃ films at different substrate temperatures (25°C, 100°C, 200°C, 250°C) using radio - frequency magnetron sputtering (RF magnetron sputtering). - **Structural Characterization**: Analyze the phase structure and microscopic morphology of the films through X - ray diffraction (XRD), scanning electron microscopy (SEM), and atomic force microscopy (AFM). - **Electrical Property Testing**: Measure the resistance - temperature relationship (ρ - T) and complex impedance spectra of the films to evaluate their NTC characteristics. ### Main Findings - **Phase Structure Change**: As the substrate temperature increases, the main phase gradually changes from BaBiO₂·₈₂ (cubic perovskite structure) to BaBiO₂·₅ (layered monoclinic structure). - **Electrical Property Optimization**: The BaBi₀·₉₂Cu₀·₀₈O₃ film deposited at 200°C exhibits the best NTC characteristics, with a room - temperature resistivity (ρ₂₅) of approximately 956 Ω·cm and a thermosensitive constant (B - value) of approximately 3480 K. - **Conduction Mechanism**: Through complex impedance spectra analysis, it is confirmed that the conduction mechanism of the film is mainly contributed by the grain resistance (Rg), rather than the grain - boundary resistance (Rgb). ### Conclusion Appropriate substrate temperature and trace copper ion doping can significantly improve the phase structure and electrical properties of Ba - Bi - O - based perovskite - type NTC thermistor films, making them have a lower room - temperature resistivity and a higher thermosensitive constant, thereby showing good NTC characteristics in practical applications. These results provide an important reference for further research and development of new - type NTC thermistor materials.