Abstract:Cu-3Ni-0.7Si-xCr-0.05Mg (x = 0.1 and 0.4) (wt% nominal composition) alloys were fabricated to investigate the effect of Cr contents on properties evolution and precipitation behavior of Cu-Ni-Si alloy. The results of the property analysis show that trace addition of 0.1 wt% Cr element contributes a better strength (ultimate tensile strength of 823 MPa) after single cold rolling and aging treatment. The precipitation behavior is characterized by transmission electron microscopy. It is found that nanoscale FCC structural Cr precipitates shift into submicron Cr 3 Si particles with Cr content increasing from 0.1 wt% to 0.4 wt%. Meanwhile, such superior formation of Cr 3 Si particle decreases the fraction of δ-Ni 2 Si owing to quick consumption of Si element from Cu matrix. Further quantitative analysis of various strengthening mechanisms reveals that the changed precipitation behavior notably affects their strengthening contribution to Cr contained alloys, resulting in an increase of more than 5.6% in the Orowan-Ashby mechanism. Surprisingly, in the case of the aging state at a temperature of 460 °C for a duration of 2 h, it is confirmed that although a much larger strengthening effect origins from nanosized δ-Ni 2 Si precipitate, the strength variation relies more on the Cr precipitation. That is, the lower strength at higher Cr content is mainly caused by the lower strengthening effect from Cr element related phases. In addition, the effect of the addition of trace Cr element on the operating mechanism on conductivity is also clarified. The results are expected to provide an appropriate content of Cr element and a dependable processing theory guidance for improving the comprehensive properties of the Cu-Ni-Si alloys.

Simultaneously enhancing the strength and electrical conductivity of Cu-Ni-Sn alloy through plastic deformation of an intermetallic compound

Accelerating Discontinuous Precipitation to Increase Strength by Pre-Deformation in Cu-Ni-Si Alloys

The Effect of Al on Microstructure and Properties of Cu-15Ni-8Sn During the Aging

Reforming Nanostructured CuAg Alloy to Improve Ductility and Electrical Conductivity

Increasing strength and conductivity of Cu alloy through abnormal plastic deformation of an intermetallic compound

Abnormally high work hardening ability and excellent comprehensive properties of copper alloys due to multiple twins and precipitates

Effects of Pre-Deformation on Precipitation Behaviors and Properties in Cu-Ni-Si-Cr Alloy

Simultaneously enhancing the strength and ductility of Cu-Ti-Fe alloy through electric current pulse induced precipitation

Excellent Mechanical Properties and High Electrical Conductivity of Cu-Co-Si-Ti Alloy Due to Multiple Strengthening

Effect of G-phase and heterogeneous deformation-induced strengthening on the mechanical properties of Cu-20Ni-20Mn-2Fe-1Si alloy

Revealing the Effect of Phase Composition and Transformation on the Mechanical Properties of a Cu–6Ni–6Sn–0.6Si Alloy

Achieving high strength and high conductivity synergy through hierarchical precipitation stimulated structural heterogeneities in a Cu-Ag-Zr alloy

Microstructure and Property Evolution of Cu–9Ni–6Sn-xCr Alloys During Thermo-Mechanical Treatment Process

Nanoprecipitates Induced Dislocation Pinning and Multiplication Strategy for Designing High Strength, Plasticity and Conductivity Cu Alloys

Effects of cold deformation and aging on the phase transformation and mechanical properties of a Cu-15Ni-8Sn alloy

Microstructure and Precipitate's Characterization of the Cu-Ni-Si-P Alloy

Enhanced mechanical properties and strengthening mechanism of Cu-Ni-Si alloy with trace chromium addition

Enhanced high-temperature mechanical properties of the Cu–1.16Ni–0.36Cr alloy owing to interactions between metastable precipitates and dislocations

Enhancing the strength of Sc-containing Al-Cu-Li alloys by modifying the precipitation behavior through plastic deformation and heat treatment

Accelerating heterogeneous nucleation to increase hardness and electrical conductivity by deformation prior to ageing for Cu-4 at.% Ti alloy

Microstructure and hot deformation behavior of the Cu-1Ni-0.9Sn-0.5Ti-0.3Cr alloy