Abstract:Repetitive upsetting-extrusion (RUE) is known as a processing method that effectively improves the properties of a billet without changing its initial shape. In this paper, one pass RUE with reduced deformation temperature (re-upsetting at 360 °C and secondary extrusion at 340 °C) and different extrusion speeds (0.5 and 1 mm/s) is implemented to improve the strength and toughness of AZ80 Mg rods, and simultaneous reduction in tensile anisotropy is achieved. Influences of one pass RUE method on the resulting microstructure and texture evolution of the alloy are investigated alongside their correlated impact on its mechanical properties. After RUE processing, the grain structure of AZ80 alloy is characterized by numerous fine dynamic recrystallized (DRXed) grains, combined with large unDRXed grains obtained at high extrusion speed or coarse DRXed grain bands obtained at low extrusion speed. Besides, β-Mg17Al12 particles dynamically precipitated during deformation, acting as strong barrier against grain boundary migration through pinning effect. Through introduction of an interactive stress state, the RUE process promotes dispersion of the fiber texture that typically develops during the extrusion process. The key factor that promotes weakening of the fiber texture is derived from the refinement of basal orientated deformed grains, which form during upsetting deformation, into numerous non-basal orientated DRXed grains during early-stage extrusion. Compared with coarse deformed grains, these fine DRXed grains delay transformation of texture into the typical [10-10]–[11-20] fiber component. Grain refinement is implicated as the most significant factor with respect to simultaneous improvement of strength and toughness in the extruded rods, while tensile yield anisotropy in response to loading along the ED and TD is attributed to unDRXed grains with [10-10] fiber orientation. Compared to the as-cast state, extruded rods demonstrate increases in yield strength, ultimate tension strength, and elongation maximally up to ~2.6, ~2.2, and ~4.9 times, respectively. And when complete DRX structure is nearly achieved, the tensile yield anisotropy of extruded bar is effectively eliminated because the refined grains with relatively dispersed orientation inhibit the nucleation of tension twin and simultaneous enhance the Hall-Petch effect.

The effect of processing parameters on the microstructure and texture evolution of a cup-shaped AZ80 Mg alloy sample manufactured by the rotating backward extrusion

An Investigation on the Microstructure and Texture of an AZ80 Cup-Shaped Piece Processed by Rotating Backward Extrusion

The evolution of microstructure and texture of AZ80 Mg alloy cup-shaped pieces processed by rotating backward extrusion

Refining the microstructure and modifying the texture of the AZ80 alloy cylindrical tube by the rotating backward extrusion with different rotating revolutions

Effect of Temperature and Revolution on the Microstructure, Texture and Microhardness of the AZ80 Alloy Cup Prepared by Rotating Backward Extrusion

Effects of die motion parameters on the microstructures and mechanical properties of rotary backward extruded AZ80 alloys

The microstructure evolution, texture weakening mechanism and mechanical properties of AZ80 Mg alloy processed by repetitive upsetting-extrusion with reduced deformation temperature

Microstructure and mechanical properties of GW83 alloy prepared by rotating backward extrusion

Microstructure and Texture Evolution of Mg-Gd-Y-Zr Alloy during Reciprocating Upsetting-Extrusion

Texture Weakening and Grain Refinement Behavior of the Extruded Mg-6.03Zn-0.55Zr Alloy During Hot Plane Strain Compression

Evolution of microstructure, texture and mechanical properties of AZ80 Mg alloy tubular produced by rotating backward extrusion with modified open punch

Study of rotational dynamic recrystallization during warm compression of an Mg-Zn-Nd-Zr alloy

High elongation heterostructure rare earth magnesium alloy based on rotating backward extrusion process

Revealing the microstructure, texture evolution and mechanical properties along the whole wall of Mg-Gd-Y-Zn-Zr cylinders by tailoring rotary backward extrusion parameters

Effects of Dynamic Recrystallization in Extruded and Compressed Az31 Magnesium Alloy

Evolution of Texture and Mechanical Anisotropy of Mg-13Gd-4Y-2Zn-0.5Zr Sheet Produced by Rotary Forward Extrusion

Deformation behaviour, microstructure evolution and dynamic recrystallization mechanism of AZ31 magnesium alloy under co-extruded by Mg-Al composite billet

Evolution of Microstructure, Texture and Mechanical Properties of ZK60 Magnesium Alloy in a Single Rolling Pass

Effect of extrusion temperature on microstructure, mechanical properties, and deformation mechanism of Mg-2.5Er-0.6Zr alloy

Effect of Double Plastic Deformation on Microstructure and Mechanical Properties of High-Content Rare-Earth AZ61 Mg Alloy

Correlation Between Dynamic Recrystallization and Formation of Rare Earth Texture in a Mg-Zn-Gd Magnesium Alloy During Extrusion