Josephson-like Colossal Resistive Switching in Nanocrystalline Y-Ba-Cu-O at Room Temperature

Guanmei Wang,Mark J. Raine,Damian P. Hampshire

DOI: https://doi.org/10.48550/arXiv.1602.00271

2016-01-31

Superconductivity

Abstract:In this paper, we present data for two nanocrystalline YBa2Cu3O7-x (YBCO) samples which both exhibit Josephson-like Colossal Resistive Switching (JCRS) in voltage-current (V-I) traces from 4.2 K up to room temperature, in magnetic fields up to 8 T. We report Josephson-like hysteresis for both positive and negative current that has not been observed before in colossal resistive switching materials. Non-zero resistance was measured in transport measurements at all temperatures. At low temperatures (< 90 K), we also observed the usual properties for YBCO including weak superconducting and paramagnetic behavior, measured using ac susceptibility and magnetization measurements. The resistivity of these nanocrystalline samples is 3 orders of magnitude higher than standard polycrystalline materials at 300 K and the temperature dependence semiconductor-like. We cannot rule out the possibility that these materials contain a superconducting component responsible for the JCRS behavior at room temperature.