Abstract:The Cu2Se compound possesses extraordinary thermoelectric performance at high temperatures and shows great potential for the application of waste heat recycling. However, a thermoelectric device usually undergoes mechanical vibration, mechanical and/or thermal cycling, and thermal shock in service. Therefore, mechanical properties are of equal importance as thermoelectric performance. However, the mechanical performance and stability of the Cu2Se compound during long-term service at high temperatures have rarely been reported. In this study, we systematically investigated the mechanical properties of Cu2Se compounds synthesized by three varied methods (melting (M), self-propagating high-temperature synthesis (SHS), and a combination of SHS and ultrasonic treatment (UT)) and investigated the thermal stability of the SHS-UT compound under different annealing temperatures. The SHS-UT process effectively refines the grain size from 19 μm for the melting sample to 5 μm for the SHS-UT sample. The high density of grain boundaries in the SHS-UT sample effectively dissipates the energy of crack propagation; thus, the mechanical properties are greatly improved. The compressive strength, bending strength, and Vickers hardness of the SHS-UT sample are 147 MPa, 52.6 MPa, and 0.46 GPa, respectively, which are 21.5, 16.6, and 35.3% higher than those of the melting sample, respectively. Moreover, excellent thermal stability is achieved in the compound prepared by SHS and ultrasonication at a temperature below 873 K. After annealing at temperatures up to 873 K for 7 days, the excellent thermoelectric performance of the Cu2Se compound is well maintained with a ZT value exceeding 1.80 at 873 K. However, with further increasing the annealing temperature to 973 K, the volatilization of Se and the precipitation of Cu result in the instability and significantly deteriorated thermoelectric performance of the material. This work provides an avenue for boosting the mechanical properties and commercial application of Cu2Se.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c12533.Experimental section (synthesis process, characterization of structure and composition, and measurement of mechanical properties and thermoelectric transport properties); compressive strength–displacement curves, flexural strength–displacement curves, and fracture strength–displacement curves for all samples; FESEM images of fracture structures for all samples; cycling tests for SHS-UT Cu2Se bulk; X-ray diffraction patterns of the SHS-UT Cu2Se sample before and after the annealing process; and density, relative density, and averaged atomic ratio for SHS-UT Cu2Se bulks before and after the annealing process (PDF)This article has not yet been cited by other publications.

Thermoelectric properties and service stability of Ag-containing Cu2Se

Enhanced Stability and Thermoelectric Performance in Cu 1.85 Se-Based Compounds

Incommensurately Modulated Structure in AgCuSe‐Based Thermoelectric Materials for Intriguing Electrical, Thermal, and Mechanical Properties

Enhanced Thermoelectric Properties of Cu2SnSe3-Based Materials with Ag2Se Addition

Thermoelectric Ag 2 Se: Imperfection, Homogeneity, and Reproducibility

Thermoelectric Properties of Strained -Cu<sub>2</sub>Se

Thermoelectric properties and thermal stability of Cd-doped Cu 2 Se thermoelectric materials

Enhanced thermoelectric properties of Cu-Se system via bond-structure adjustment by Ag-doping

Investigation on Low-Temperature Thermoelectric Properties of Ag2Se Polycrystal Fabricated by Using Zone-Melting Method

Mechanical Properties and Thermal Stability of the High-Thermoelectric-Performance Cu 2 Se Compound

Thermoelectric performance of copper-rich β-Cu2Se films with Ag-doping by magnetron sputtering

Entropy and Enthalpy Co‐Tuning Strategy in Cu2‐yAgy(In0.06Sn0.94)Se2S System toward Excellent Thermoelectric Performance

Low thermal conductivity and high thermoelectric performance in Cu2Se/CuAgSe composite materials

Enhancement of the Thermoelectric Performance of Cu 2 GeSe 3 via Isoelectronic (Ag, S)-co-substitution

The electronic-thermal transport properties and the exploration of magneto-thermoelectric properties and the Nernst thermopower of Ag2(1+)Se

Effect of ball milling time on the formation and thermal properties of Ag2Se and Cu2Se compounds

Prefer‐Oriented Ag2Se Crystal for High‐Performance Thermoelectric Cooling

Cu2−xS and Cu2−xSe Alloys: Investigating the Influence of Ag, Zn, and Ni Doping on Structure and Transport Behavior

Altering the high-temperature stability and thermoelectric properties of Cu1.8S thermoelectric materials by Se incorporation

Ag Interstitial Inhibition and Phonon Scattering at the ZnSe Nano-Precipitates to Enhance the Thermoelectric Performance of Ag 2 Se

Stabilization and high thermoelectric performance of high-entropy-type cubic AgBi(S, Se, Te)2