Abstract:In this work, lithium aluminosilicate (LAS) glass-ceramics were prepared from lithium disilicate glass powder and mullite whiskers. Lithium disilicate glass powder (28.6Li-68.6Si-2K-0.8La, mol.%) with contents of 5, 10 and 15 wt.% mullite whiskers were hot-pressed at 860 °C for 1 h. The effects of added mullite on phase composition, microstructure, mechanical properties, coefficient of thermal expansion (CTE) and translucency were systematically studied. Also, the mechanism for phase transformation and grain growth was discussed. The LAS glass-ceramic samples exhibited relative densities above 98% with main crystalline phases of lithium disilicate (Li2Si2O5, LD), lithium silicate (Li2SiO3, LM), and β-spodumene (LiAlSi2O6). The β-spodumene whiskers were in-situ synthesized through the reaction between mullite whiskers and glass matrix. As β-spodumene fraction rose, lithium disilicate crystals content decreased and that of lithium silicate increased, resulting in declined bending strength and improved fracture toughness. The composite containing 10 wt.% mullite whisker showed optimal performance with bending strength above 300 MPa and fracture toughness of 2.7 MPa·m1/2. The formation of β-spodumene in the obtained composite declined CTE, with values ranging from 10.5×106 °C-1 for LD glass-ceramic to 6.03×10-6 °C-1 for LAS glass-ceramic doped with 15 wt.% mullite whiskers. Finally, though the real in-line transmission of obtained glass-ceramic composites declined as β-spodumene content rose, the specimens containing less than 10 wt.% mullite whiskers showed favorable translucency, which would suit applications in dental restoration.

Permeability and thermal expansion properties of porous LAS ceramic prepared by gel-casting method

Highly Porous LAS-SiC Ceramic with Near-Zero Thermal Expansion Prepared Via Aqueous Gel-Casting Combined with Adding Pore-Forming Agents

Sintering Behaviors, Microstructure and Properties of Li2O-Al2O3-SiO2 Glass-ceramics for LTCC Applications

Effect of LiAlSiO4 Particle Size on the Properties of LAS/SiC Porous Ceramics with Near Zero Thermal Expansion

Effect of glassy bonding materials on the properties of LAS/SiC porous ceramics with near zero thermal expansion

Effects of Solid Content on the Phase Assemblages, Mechanical and Dielectric Properties of Porous Α-Sialon Ceramics Fabricated by Freeze Casting

Mechanical and Thermal Properties of Graphene Nanoplates (gnps)/lithium Aluminosilicate (LAS) Composites: an Analysis Based on Mathematical Model and Experiments

Porous Si3N4 Ceramics Prepared by TBA-based Gel-casting

Mechanical and dielectric properties of porous Si3N4 ceramics prepared by modified water‐based gel casting

Preparation of calcium hexaluminate porous ceramics by gel-casting method with polymethyl methacrylate as pore-forming agent

Effect of Al(OH) 3 on the Properties of Silica-based Ceramic Cores Prepared by Laser Powder Bed Fusion Combined with Vacuum Infiltration

Microstructure and thermal properties of binary ceramic particle-reinforced aluminum matrix composites with SiC/LAS

Air permeable alumina-based porous ceramics with high performance prepared by novel gel casting route

Pore Architectures And Mechanical Properties Of Porous -Sialon Ceramics Fabricated Via Unidirectional Freeze Casting Based On Camphene-Templating

Effects of Pore-Forming Agent Content on the Properties of Porous 8ysz Ceramics by Tba Based Gel-Casting

Influences of Al2O3 content on crystallization and physical properties of LAS glass-ceramics prepared from spodumene

Effect of Boron Doping on Fracture Behavior of Carbon Fiber Reinforced Lithium Aluminosilicate Glass Ceramics Matrix Composites

Pore Architectures and Mechanical Properties of Porous α-SiAlON Ceramics Fabricated via Unidirectional Freeze Casting Based on Camphene-Templating

Effect of Added Mullite Whisker on Properties of Lithium Aluminosilicate (LAS) Glass-Ceramics Prepared for Dental Restoration.

Porous Si3N4 ceramics with hierarchical pore structures prepared by gelcasting using DMAA as gelling agent and PS as pore–forming agent

Enhancing the thermal insulating properties of lanthanum zirconate porous ceramics via pore structure tailoring