Abstract:Nitrogen-rich ultra-thin (1-2 nm thick) layers in diamond produced by high-temperature nitrogen ion (N2+) implantation at low N2+ energies studied by in situ x-ray photoelectron spectroscopy are reported. Nitrogen bonding at the subsurface region and its thermal stability, as well as structural defects in polycrystalline diamond (PCD) implanted with 200, 500, and 800 eV N2+ at room temperature (RT) and 600 °C at an ion dose of 4.5 × 1014 ions/cm2, are investigated. Implantation at RT leads to nitrogen bonding at interstitial and substitutional sites in the diamond lattice, which is associated with the C-N/C=N bond, lower intensity of the C≡N (nitrile-like) component associated with nitrogen bonding with carbon defects, and quaternary nitrogen. The relative composition of these chemical states varies with implantation energy, temperature, and post-implantation annealing temperature. Upon annealing the RT implanted layers above 500-600 °C, the interstitial nitrogen converts to substitutional nitrogen. This process competes with nitrogen desorption. The thermal stability of nitrogen increases with implantation energy. Implantation at 600 °C at 800 eV resulted in a significantly lower concentration of nitrile-like bonds and a lower density of structural defects compared to RT implantation at the same energy. These effects are associated with dynamic annealing, which becomes more significant at higher implantation energies. Upon high-temperature implantation, nitrogen mostly populates directly substitutional sites. Nitrogen implantation at low energy and high temperature may be a viable way to nitride diamond surfaces with reduced density of defects where nitrogen is selectively bonded to substitutional sites. Finally, a comparison between nitrogen implantation into PCD and Diamond (100) [Di(100)] surfaces is presented.

Enhanced optical properties of chemical vapor deposited single crystal diamond by low-pressure/high-temperature annealing

Recent advances in high-growth rate single-crystal CVD diamond

Characterization of Nitrogen Doped Chemical Vapor Deposited Single Crystal Diamond Before and after High Pressure, High Temperature Annealing

Nano-polycrystalline diamond formation under ultra-high pressure

Enhanced Growth Of High Quality Single Crystal Diamond By Microwave Plasma Assisted Chemical Vapor Deposition At High Gas Pressures

Enhancing the mechanical properties of single-crystal CVD diamond.

Nano-crystalline Diamond Films Synthesized at Low Temperature and Low Pressure by Hot Filament Chemical Vapor Deposition

Ultrahard diamond single crystals from chemical vapor deposition

Low-Temperature Growth Of Ultra-Thin Nano-Crystalline Diamond Films By Hfcvd In A Ch4/H-2 Mixture

Developments in synthesis, characterization, and application of large, high-quality CVD single crystal diamond

Very high growth rate chemical vapor deposition of single-crystal diamond.

The Interface and Mechanical Properties of a CVD Single Crystal Diamond Produced by Multilayered Nitrogen Doping Epitaxial Growth

Effect of pressure on nanocrystalline diamond films deposition by hot filament CVD technique from CH4/H2 gas mixture

Dynamic annealing assisted near-surface structural and bond stabilization in high-temperature low-energy N2+ implanted diamond

Photothermal effects during nanodiamond synthesis from a carbon aerogel in a laser-heated diamond anvil cell

Charge transfer effects, thermo- and photochromism in single crystal CVD synthetic diamond

Single crystal diamond growth by MPCVD at subatmospheric pressures

Rapid Growth of Nanocrystalline Diamond on Single Crystal Diamond for Studies on Materials under Extreme Conditions

Homoepitaxy Growth of Single Crystal Diamond under 300 torr Pressure in the MPCVD System

Effect of Nitrogen on Growth and Optical Properties of Single-Crystal Diamond Synthesized by Chemical Vapor Deposition

Control of surface and bulk crystalline quality in single crystal diamond grown by chemical vapour deposition