Abstract:Once the characteristic size of materials reaches nanoscale, the mechanical properties may change drastically and classical mechanisms of materials failure may cease to hold. In this paper, we focus on joint atomistic-continuum studies of failure and deformation of nanoscale materials. In the first part of the paper, we discuss the size dependence of brittle fracture. We illustrate that if the characteristic dimension of a material is below a critical length scale that can be on the order of several nanometres, the classical Griffith theory of fracture no longer holds. An important consequence of this finding is that materials with nano-substructures may become flaw-tolerant, as the stress concentration at crack tips disappears and failure always occurs at the theoretical strength of materials, regardless of defects. Our atomistic simulations complement recent continuum analysis (Gao et al 2003 Proc. Natl Acad. Sci. USA 100 5597 - 600) and reveal a smooth transition between Griffith modes of failure via crack propagation to uniform bond rupture at theoretical strength below a nanometre critical length. Our results may have consequences for understanding failure of many small-scale materials. In the second part of this paper, we focus on the size dependence of adhesion systems. We demonstrate that optimal adhesion can be achieved by either length scale reduction, or by optimization of the shape of the surface of the adhesion element. We find that whereas change in shape can lead to optimal adhesion strength, those systems are not robust against small deviations from the optimal shape. In contrast, reducing the dimensions of the adhesion system results in robust adhesion devices that fail at their theoretical strength, regardless of the presence of flaws. An important consequence of this finding is that even under the presence of surface roughness, optimal adhesion is possible provided the size of contact elements is sufficiently small. Our atomistic results corroborate earlier theoretical modelling at the continuum scale (Gao and Yao 2004 Proc. Natl Acad. Sci. USA 101 7851 - 6). We discuss the relevance of our studies with respect to nature's design of bone nanostructures and nanoscale adhesion elements in geckos.

Size Selection of Crack Front Defects: Multiple Fracture-Plane Interactions and Intrinsic Length Scales

Size selection of crack front defects: Multiple fracture-plane interactions and intrinsic lengthscales

Size effects in micro and nanoscale materials fracture

Size effects in the toughening of brittle materials by heterogeneities: a non-linear analysis of front deformations

Size Effects in Layered Composites – Defect Tolerance and Strength Optimization

Finite size effects on crack front pinning at heterogeneous planar interfaces: Experimental, finite elements and perturbation approaches

Size-dependent fracture in elastomers: experiments and continuum modeling

Complexity of crack front geometry enhances toughness of brittle solids

Cracking and Adhesion at Small Scales: Atomistic and Continuum Studies of Flaw Tolerant Nanostructures

Critical crack length during fracture

Interaction of an interfacial crack with linear micro-defects under out-of-plane shear loading

Topological Defect Formation in Slow Three-Dimensional Fracture

Crack coalescence mechanism of flaw pairs under biaxial loading conditions using additively printed models and photoelastic experiments

Meso-scale size effects of material heterogeneities on crack propagation in brittle solids: Perspectives from phase-field simulations

Two Possible Defect Growth Modes in Soft Solids

Size-dependence of fracture processes in intact rocks

Facet formation in slow three-dimensional fracture

A phase field model for cohesive fracture in micropolar continua

Cooperating Cracks in Two-Dimensional Crystals

Helical crack-front instability in mixed-mode fracture

Size-dependency and lattice-discreetness effect on fracture toughness in 2D crystals under antiplanar loading