Abstract:A dual cross‐linked Zn2+‐based copolymer hydrogel is developed as a substitute for natural articular cartilage. This hydrogel exhibits outstanding mechanical strength, self‐healing capabilities, and adhesive properties, allowing seamless integration with surrounding tissue. With water content similar to natural cartilage, this hydrogel presents itself as a strong candidate for cartilage replacement applications. Hydrogels have emerged as promising candidates for biomedical applications, such as replacing natural articular cartilage, owing to their unique viscoelastic properties. However, sufficient mechanical properties, self‐healing ability, and adhesive nature are some issues limiting its application window. Here, a facile one‐pot synthesis of dual cross‐linked zinc‐coordinated copolymer hydrogels is presented. The network structure of the copolymer hydrogels is strategically developed via dynamic and reversible physical cross‐linking by Zn2+ ions and simultaneous covalent cross‐linking through a covalent cross‐linker viz methylene bisacrylamide. Fourier‐transform infrared (FTIR), X‐ray diffraction (XRD) scanning electron microscopy (SEM), and Brunauer–Emmett–Teller (BET) analysis have thoroughly characterized the structure of the synthesized hydrogels. The introduction of Zn2+ offers dynamic and reversible complexation, leading to excellent mechanical properties and self‐healing features. Moreover, the percentage of the equilibrium water content of zinc‐coordinated copolymer hydrogel samples is comparable with that of natural articular cartilage. The Shear sliding study shows the dominant adhesive behavior of HGel‐Zn(NO3)2 sample compared to the parent HGel sample. This facile dual cross‐linked hydrogel, HGel‐Zn(NO3)2, with a combination of good mechanical properties, efficient self‐recovery, adequate water content, and favorable adhesive nature, seems very promising to mimic the articular cartilage.

A dual-crosslinked zwitterionic hydrogel with load-bearing capacity and ultra-low friction coefficient

Mimicking the Mechanical Properties of Cartilage Using Ionic- and Hydrogen-Bond Cross-Linked Hydrogels with a High Equilibrium Water Content above 70%

Phospholipid reinforced P(AAm-co-AAc)/Fe3+ hydrogel with ultrahigh strength and superior tribological performance

Cartilage-inspired terpolymer hydrogel with excellent mechanical properties and superior lubricating ability

Synthesis and Characterizations of Zwitterionic Copolymer Hydrogels with Excellent Lubrication Behavior

Low coefficient of friction hydrogels with fast self-healing properties inspired by articular cartilage

High Lubricity Meets Load Capacity: Cartilage Mimicking Bilayer Structure by Brushing Up Stiff Hydrogels from Subsurface

A Synthetic Hydrogel Composite with the Mechanical Behavior and Durability of Cartilage

Fabrication of Zinc(II) Mediated Poly(Acrylamide Co Acrylic Acid) Hydrogel with Thixotropic and Tribological Properties

Double‐network polyvinyl alcohol composite hydrogel with self‐healing and low friction

Sandwich hydrogel to realize cartilage-mimetic structures and performances from polyvinyl alcohol, chitosan and sodium hyaluronate

A lubricant and adhesive hydrogel cross-linked from hyaluronic acid and chitosan for articular cartilage regeneration

Articular Cartilage Inspired Bilayer Tough Hydrogel Prepared by Interfacial Modulated Polymerization Showing Excellent Combination of High Load-Bearing and Low Friction Performance.

Bilayer Hydrogels with Low Friction and High Load-Bearing Capacity by Mimicking the Oriented Hierarchical Structure of Cartilage

Dual-physical network PVA hydrogel commensurate with articular cartilage bearing lubrication enabled by harnessing nanoscale crystalline domains

Cationic Modified PVA Hydrogels Provide Low Friction and Excellent Mechanical Properties for Potential Cartilage and Orthopedic Applications

Cartilage-Inspired, High-Strength, and Heat-Tolerant Lubricating Hydrogels by Macrophase Separation

Bionic layered hydrogel with high strength for excellent lubrication and load capacity

An ultra‐tough, creep‐resistant, wear‐resistant hydrogel for cartilage replacement

Exploring the relevance between load-bearing capacity and surface friction behavior based on a layered hydrogel cartilage prototype

Fabrication of a Double-Network Hydrogel Based on Carboxymethylated Curdlan/Polyacrylamide with Highly Mechanical Performance for Cartilage Repair