Abstract:Developing bioinspired hydrogel materials with extraordinary lubrication, load-bearing, and antiwear property is necessary for durable lubricious implants or devices. Despite the extensive research focus on lubrication of hydrogel materials, achieving a balance between lubrication and load-bearing for the current system is commonly difficult because of their poor mechanical property. Herein, a cartilage-inspired layered hydrogel material composed of a soft and porous top layer and a robust bottom layer is easily prepared by employing an alkali-induced network dissociation strategy. The thickness of the top soft layer increases with extending the alkali treatment time, along with differential surface and cross-sectional morphologies and mechanical property. The top soft and porous layer ensures that the surface shows extremely low friction (coefficient of friction (COF) ∼ 0.009, 3 N; COF ∼ 0.035, 20 N) against a hard steel ball contact pair, while the bottom layer acts as an excellent load-bearing function. Therefore, the layered hydrogels can achieve extraordinary wear resistance features, resulting from a combination of surface lubrication and bottom load-bearing. It is demonstrated that the method can be used to develop a layered hydrogel lubrication catheter, for which both of its inner and outer surfaces exhibit a slippery feature. The extraordinary lubricious performance of the layered hydrogels implies their potential application in the field of tissue engineering and medical devices.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.chemmater.0c02450?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.chemmater.0c02450</a>.COF curve of the control PAA–Fe/PAM hydrogel sheet (Figure S1); characterization of surface morphologies for the layered hydrogel samples after going through 3600 cycles sliding friction test (Figures S2 and S3); characterization of the cross-sectional morphology for the layered hydrogel sample upon encountering 50 000 cycles sliding friction test (Figure S4); the calculated static average contact pressures <i>P</i><sub>ave</sub> of the layered hydrogel sample under different load conditions (Table S1) (<a class="ext-link" href="/doi/suppl/10.1021/acs.chemmater.0c02450/suppl_file/cm0c02450_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Articular Cartilage Inspired Bilayer Tough Hydrogel Prepared by Interfacial Modulated Polymerization Showing Excellent Combination of High Load-Bearing and Low Friction Performance.

High Lubricity Meets Load Capacity: Cartilage Mimicking Bilayer Structure by Brushing Up Stiff Hydrogels from Subsurface

Bilayer Hydrogels with Low Friction and High Load-Bearing Capacity by Mimicking the Oriented Hierarchical Structure of Cartilage

Mechanically Robust Lubricating Hydrogels Beyond the Natural Cartilage as Compliant Artificial Joint Coating

Microgel-Modified Bilayered Hydrogels Dramatically Boosting Load-Bearing and Lubrication

Dual-physical network PVA hydrogel commensurate with articular cartilage bearing lubrication enabled by harnessing nanoscale crystalline domains

Cartilage-inspired terpolymer hydrogel with excellent mechanical properties and superior lubricating ability

Bioinspired polymer-incorporating self-lubricating and antifouling hydrogels

Vertical and Horizontal Double Gradient Design for Super‐Slippery and High‐Bearing Hydrogel Skeleton

Exploring the relevance between load-bearing capacity and surface friction behavior based on a layered hydrogel cartilage prototype

Bionic layered hydrogel with high strength for excellent lubrication and load capacity

PVA-BA/PEG hydrogel with bilayer structure for biomimetic articular cartilage and investigation of its biotribological and mechanical properties

Bioinspired Design of a Cartilage-like Lubricated Composite with Mechanical Robustness

Biomimetic Layered Hydrogel Coating for Enhanced Lubrication and Load-Bearing Capacity

A dual-crosslinked zwitterionic hydrogel with load-bearing capacity and ultra-low friction coefficient

Layered Hydrogel with Controllable Surface Dissociation for Durable Lubrication

Sandwich hydrogel to realize cartilage-mimetic structures and performances from polyvinyl alcohol, chitosan and sodium hyaluronate

Mimicking the Mechanical Properties of Cartilage Using Ionic- and Hydrogen-Bond Cross-Linked Hydrogels with a High Equilibrium Water Content above 70%

Bio-inspired hydrogel-polymer brush bi-layered coating dramatically boosting the lubrication and wear-resistance

Cartilage-bone inspired the construction of soft-hard composite material with excellent interfacial binding performance and low friction for artificial joints

A Janus hydrogel material with lubrication and underwater adhesion