Abstract:The failure of plasma-sprayed thermal barrier coatings (TBC) usually occurs through spalling of ceramic coating. The crack evolution during thermal cycling of TBC is directly associated with its spalling. In this paper, the cracks in TBC along the direction of the interface between ceramic coating and bond coat were examined from cross-section of TBC experienced different numbers of thermal cycle, and crack number and the total length of cracks were measured to aim at understanding the failure mechanism. TBC consists of cold-sprayed NiCoCrAlTaY bond coat on IN738 superalloy and double layered plasma-sprayed 8YSZ with a columnar grain structured YSZ interlayer of about 20 μm thick and about 230 μm lamellar YSZ. With each isothermal cyclic test, the TBC samples were kept at 1150 °C for 26 min hold and then cooled down to a temperature less than 80 °C in 4 min by air forced cooling. Results showed that cracks propagated primarily within lamellar-structured YSZ over the columnar YSZ along lamellar interface. The measurement from the cross-section revealed that crack number and total crack length apparently increased with the increase of the number of thermal cycle. It was found that cracks with a length less than a typical size of 200 μm accounted for the majority of cracks despite the number of thermal cycle during the test. A crack initiation and propagation model for plasma-sprayed TBC is proposed with a uniform distribution of circular cracks. The propagatable cracks form homogeneously within plasma-sprayed porous YSZ coating at the early stage of thermal cycling and propagate at an identical rate during thermal cycling. Only a few of large cracks are formed before most cracks reach to the critical size for multi-cracks linking-up. The propagation of most cracks to the critical size will leads to the rapid crack bridging and subsequent spalling of top ceramic TBC.

Microstructural Evolution and Failure Mechanisms of Thermal Barrier Coatings under Extreme Environmental Conditions

LC/8YSZ TBCs Thermal Cycling Life and Failure Mechanism under Extreme Temperature Gradients

Failure of Electron Beam Physical Vapor Deposited Thermal Barrier Coatings System under Cyclic Thermo-Mechanical Loading with a Thermal Gradient

Sintering-induced delamination of thermal barrier coatings by gradient thermal cyclic test

Failure behaviour of EB-PVD YSZ thermal barrier coatings under simulated aero-engine operating conditions

Failure Mechanism and Cracking-Resistant Design of Thermal Barrier Coatings with Long Life Span

Thickness-related failure behaviors of the thermal barrier coatings under thermal gradient cycling

Failure behavior study of EB-PVD TBCs under CMAS Corrosion and Thermal Shock Cycles

Experimental Study on the Interfacial Delamination in a Thermal Barrier Coating System at Elevated Temperatures

GdYbZrO thermal barrier coatings by EB-PVD: Phase, microstructure, thermal properties and failure

Thermal shock life and failure behaviors of La2Zr2O7/YSZ, La2Ce2O7/YSZ and Gd2Zr2O7/YSZ DCL TBCs by EB-PVD

Thermal shock resistance and failure analysis of La2(Zr0.75Ce0.25)2O7-based TBCs produced by atmospheric plasma spraying

Failure Mechanism of EB-PVD Thermal Barrier Coatings under the Synergistic Effect of Thermal Shock and CMAS Corrosion

Failure Characteristics and Life Prediction for Thermally Cycled Thermal Barrier Coatings

Failure Behavior Study of EB-PVD TBCs under Salt Spray Corrosion and Thermal Shock Cycles

Thermal shock behaviors and failure mechanisms of EB-PVD thermal barrier coatings using radiant heating

Sintering and Failure Behaviour of Eb-Pvd Thermal Barrier Coating after Isothermal Treatment

Multi-layered Thermal Barrier Coatings Fabricated by Plasma-Spraying and Dry-Ice Blasting: Microstructure Characterization and Prolonged Lifetime

Evolution of Lamellar Interface Cracks During Isothermal Cyclic Test of Plasma-Sprayed 8YSZ Coating with a Columnar-Structured YSZ Interlayer

Thermal cycling performance of GYbZ/YSZ thermal barrier coatings with different microstructures based on finite element simulation

LaYbZrO thermal barrier coatings by EB-PVD: Microstructure, thermal shock life and failure behaviors