Abstract:The biodegradable metallic devices undergo stress/strain-induced corrosion when they are used for load-bearing applications. The stress/strain induced-corrosion behavior causes differences in corrosion rate, corrosion morphology, strain distribution and mechanical performance of the devices. One representative example is the biodegradable stent. Biodegradable stents undergo complex inhomogeneous deformation that can cause dramatic non-uniform stent degradation, resulting in stress concentration and stents failure. The degradation of biodegradable devices requires special attention to the mutual effect between the applied strain and degradation.The quantitative relationship between strain and corrosion of the sample alloys (WE43, Fe and Zn), selected from three typical biodegradable metals, is firstly investigated and compared in this study. The in vitro degradation and the strength retention of WE43, Fe and Zn wires were investigated under different elastic and plastic strain levels ranging from 0.1% to 30%. The results indicated that the applied strain could bring down the corrosion potential, increase corrosion current and accelerate the degradation of three biodegradable metals. Specifically, remarkable enhanced localized corrosion was observed for plastic strained WE43 compared with those with elastic strains. This localized corrosion morphology significantly accelerated the strength decline at first, while the differences diminished with longer immersion period. Fe and Zn exhibited increased degradation with plastic strain applications than those under elastic strains. However, the degradation was not further increased with the increasing magnitude of plastic strains. Moreover, the bended wires were subcutaneously implanted in the dorsal aspect of the rats and the effect of bending deformation on in vitro and in vivo degradation of three metallic wires were also compared. The U-bended WE43 wires suffered more severe in vitro degradation at the stress concentrated region. Surprisingly, the early fracture of the undeformed regions was observed in the in vivo test. In conclusion, the corrosion rate, corrosion morphology and mechanical properties of WE43, Fe and Zn was sensitive to magnitude of the applied strains. The quantification results provided new insights into understanding the strain-dependent corrosion of three biodegradable metals both in vitro and in vivo.

Effects of Compressive Stress on the Corrosion Behavior of Biodegradable Zinc with Tension-Compression Asymmetry under Simulated Physiological Environment

Effect of strain on degradation behaviors of WE43, Fe and Zn wires

Effects of Dynamic Flow Rates on the In Vitro Bio-Corrosion Behavior of Zn-Cu Alloy

Research on elastic recoil and restoration of vessel pulsatility of Zn-Cu biodegradable coronary stents

Study on mechanical and degradation behavior of Zn–Mn-xMg alloys under coupling effects of stress and SBF

Investigating the Stress Corrosion Cracking of a Biodegradable Zn-0.8 Wt%li Alloy in Simulated Body Fluid

Exploring the Biodegradation of Pure Zn under Simulated Inflammatory Condition

Monotonic and fatigue behavior of steel-concrete composite beams subjected to corrosion

Compressive Behaviour of Corroded Thin-Walled Circular Section Steel Stub Columns

In vitro bio-corrosion behaviors of biodegradable AZ31B magnesium alloy under static stresses of different forms and magnitudes

Insight into the corrosion behaviour and degradation mechanism of pure zinc in simulated body fluid

Effects of bovine serum albumin on the corrosion behavior of biodegradable Zn–Cu alloy under dynamic flowing conditions

The compressive stress effect on fatigue crack growth under tension–compression loading

Corrosion Behavior and Mechanical Integrity of Zn-based Guided Bone Generation (GBR) Membrane Subjected to U-bending Deformation

Insights into the Influence of Tensile and Compressive Strain on the Microstructure and Corrosion Performance of 304 L Stainless Steel

Experimental study and finite element analysis of degradation behavior of epoxy zinc-rich coating system under stress corrosion

The stress corrosion cracking behaviour of biomedical Mg-1Zn alloy in synthetic or natural biological media

Corrosion of high-strength steel in 3.5% NaCl solution under hydrostatic pressure: understanding electrochemical corrosion with tensile stress coupling

Degradation Behavior of Zn–Cu Stents with Different Coatings in Sodium Chloride Solution

Effect of Pre-strain on Microstructure and Corrosion Behavior of a Novel High-Zn Containing Al-Zn-Mg-Cu Alloy

Enhanced Experimental Setup and Methodology for the Investigation of Corrosion Fatigue in Metallic Biodegradable Implant Materials