Abstract:Microstructure, texture evolution and mechanical properties of extruded Mg-4.58Zn-2.6Gd-0.18Zr alloy were investigated at extrusion temperatures of 260 °C, 280 °C and 300 °C, extrusion ratios of 10, 15 and 30, and ram speeds of 3 mm s−1 and 6 mm s−1, respectively. The results indicated that the as-cast experimental alloy was composed of α-Mg matrix, coarse α-Mg + W(Mg3Zn3Gd2) eutectic and icosahedral quasicrystalline I(Mg3Zn6Gd) phase. A small amount of undissolved W phases were detected after the homogenization treatment at 505 °C up to 16 h, while most I phase dissolved into the α-Mg matrix. The initial crystallites before extrusion were randomly oriented, and showed a typical random texture. After extrusions, all samples exhibited a bimodal microstructure consisting of fine Dynamic recrystallization (DRX) grains and coarse elongated un-DRX grains, and the formation of ultra-fine DRX grains only occurred in the sample with an extrusion ratio of 10 at 260 °C, 3 mm s−1, which was caused by the solute segregation in homogenized billets and non-uniformly distributed W phase during the extrusion process. A fiber texture with {0002} planes and <1̄21̄0> directions paralleled to the extrusion direction was observed to be dominant in all the extruded samples. Furthermore, the increase of extrusion ratio was found to be beneficial for the DRX process and refinement of grain size, and the maximum texture intensity was accordingly weakened, which resulted in a decrease of tensile yield strength but an increase of elongation. With increasing the extrusion temperature or ram speed, both the grain size and DRX fraction gradually increased. Consequently, the texture was randomized and the maximum texture intensity decreased, which led to a reduction of the elongation and tensile yield strength. The tensile failure behaviors under different extrusion conditions were found to be related with the contraction twin lamellas formed in the un-DRX grains and the string-like W phases.

Achieving High Strength-Ductility Synergy in Mg-Gd-Zn-Zr Alloy by Controlling Extrusion Processes Parameters

Numerical and Experimental Investigation on Hot Backward Extrusion Process of Mg-Gd-Y-Zn-Zr Magnesium Alloy

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

Evolution of Bimodal-Structure and Achieving Ultra-High Yield Strength in the As-Extruded ZK70 Alloy Via Gd Addition

Microstructure and Mechanical Properties of Moderate-Speed Extrudable Mg-Gd-Sm-Zr Alloy

Achieving High Strength-Ductility Synergy in a Dilute Mg-Gd-Zn-Zr Alloy with Heterogeneous Structure Via Hot Extrusion

Manufacturing High-Performance Mg Alloy Through Hot Extrusion

Microstructure and mechanical properties of Mg-Gd-Zn-Zr alloy after hot extrusion

Effect of Extrusion Parameters on Microstructure and Mechanical Properties of Mg-6Zn-1Mn-0.2Gd Alloy

Influence of Extrusion Conditions on Microstructure and Mechanical Properties of Mg-2Gd-0.3Zr Magnesium Alloy

Tailoring The Strength And Formability Of Mg Alloys Through Rare Earth Element Additions (Gd And Dy) And Dynamic Recrystallizations

Microstructure Evolution and Mechanical Properties of the Mg-Sm-Gd-Zn-Zr Alloy During Extrusion

Effect of Extrusion Parameters on Microstructure and Mechanical Properties of Mg-7.5Gd-2.5Y-3.5Zn-0.9Ca-0.4Zr (wt%) Alloy

Microstructures and Mechanical Properties of Mg-10Gd-3Y-2Zn-0.5Zr Alloy

Effects of extrusion process on microstructure, precipitates and mechanical properties of Mg-Gd-Y-Zr-Ag alloys

Microstructures and Mechanical Properties of Mg-Gd-Y-(Mn, Zr) Magnesium Alloys

High Performance Mg Alloy with Designed Microstructure and Phases

Excellent Strength-Ductility Synergy Properties of Mg-Sn-Zn-Zr Alloy Mediated by a Novel Differential Thermal ECAP (DT-ECAP)

Microstructure, Texture Evolution and Tensile Properties of Extruded Mg-4.58Zn-2.6Gd-0.16Zr Alloy

Influence of Extrusion Ratio on Microstructure and Tensile Properties of Mg–Gd–Y–Zn–Zr Alloy

Microstructure and Strengthening Mechanism of High Strength Mg–10Gd–2Y–0.5Zr Alloy