Abstract:Studying the fretting wear mechanism of zirconium alloy in high temperature high pressure water is of great importance for understanding the failure behavior of fuel assembly. In this work, the tangential fretting wear of zirconium alloy tube at different displacement amplitudes (40 mu m and 80 mu m) and normal forces (6 N and 12 N) was investigated in high temperature high pressure water. The results show that the wear depth and wear volume of zirconium alloy tested at 6 N-80 mu m are the highest among all the tests. When the testing condition is 6 N-80 mu m, the fretting is located in the gross slip regime. Oxidation and abrasive wear dominate the fretting wear behavior. The increase in normal force and decrease in displacement reduces the relative sliding distance between the contact interfaces, which reduces the ejection of wear debris and changes the wear mechanism. When the test conditions are 6 N-40 mu m and 12 N-40 mu m, the fretting regime is located in the partial slip regime, and the dominant wear mechanisms are adhesive wear and oxidation. Under the synergistic effect of mechanical wear and high-temperature water corrosion, a dual-layer structure oxide scale is formed on the worn area. The mixed oxide layer with loose and porous structure is formed by the accumulation of granular wear debris, while the dense inner oxide layer is mainly formed by oxidation of the matrix alloy. Fretting wear accelerates material corrosion by wear debris refinement and cracking. The integrity of the oxide layer is negatively correlated with its thickness. As the thickness of the oxide layer increases, more cracks can be observed in the oxide layer.

Evolution of Fretting Wear Behavior of Zirconium Alloy Cladding Tube under Gross Slip Regime in Simulated Primary Water of Pressurized Water Reactor

Fretting Wear Behaviour of Zr Alloy Cladding Tube under Partial Slip Regime with Different Duration in Simulated Primary Water of Pwr

Fretting Wear Behavior of Zr Alloy Cladding Tube Mated with Zr Alloy Dimple under Mixed Fretting Regime in Simulated Primary Water of PWR

Effects of displacement amplitude and normal force on fretting wear behavior of zirconium alloy tube in simulated primary water of PWR

Effect of Normal Force on Fretting Wear Behavior of Zirconium Alloy Tube in Simulated Primary Water of PWR

Establishment of Fretting Maps of Zr Alloy Cladding Tube Mated with Zr Alloy Dimple in Simulated Primary Water of Pressurized Water Reactor

The Transformation of Fretting Corrosion Mechanism of Zirconium Alloy Tube Mating with 304 Stainless Steel in High Temperature High Pressure Water

Fretting corrosion behavior and microstructure evolution of hydrided zirconium alloy under gross slip regime in high temperature high pressure water environment

Wear Behaviour and Microstructural Changes of SiCw-Al Composite under Unlubricated Sliding Friction

Fretting Wear Behavior of Zirconium Alloy in B-Li Water at 300 °C

Characterization and fretting wear behavior of zirconium alloy treated in high temperature water

Study on the fretting wear performance of oxide layer and Cr coating on zirconium alloy in high-temperature water

Effect of temperature on the fretting wear behavior of Cr-coated Zircaloy cladding in high-temperature pressurized water

Effect of Micro-Arc Oxidation on Fretting Wear Behavior of Zirconium Alloy Exposed to High Temperature Water

Fretting Corrosion-Induced Microstructural Evolution of Alloy 690TT Tube in High Temperature Pressurised Water

Autoclave grid-to-rod fretting corrosion behaviors of the Zr alloy fuel cladding with and without Cr coating through advanced characterization

Understanding the fretting corrosion mechanism of zirconium alloy exposed to high temperature high pressure water

Understanding the Microstructure Evolution of Ni-Based Superalloy Within Two Different Fretting Wear Regimes in High Temperature High Pressure Water

Fretting corrosion running regime and damage mechanism evolution of zirconium alloy mated with Inconel 718 alloy in high temperature high pressure water environment

Stress-dependent subsurface structural transformations of gradient nanograin Ti-6Al-4V alloy and its impact on wear behavior

Study on Bi-directional Composite Fretting Wear Characteristics of Zr-4 Alloy Tube with Different Phase Differences under Temperature Conditions