Abstract:In this work, hydrogen charged Zircaloy-4 has been investigated under an in-situ electron backscatter diffraction during tensile loading. Aim were, first, to distinguish the hydride phase type and its spatial distribution, second to determine hydride phase transformation (HPT) and orientation relationship (OR) subjected to uniaxial tensile condition, and third to correlate the hydrides evolution and their effect on the micromechanical behavior, such as slip mode activation and lattice rotation, of Zircaloy-4. Apart from the applied stress, the analysis reveals that hydride reorientation is strongly related to temperature and loading mode. We noted that deformation induced δ-ZrH 1.5 transformed to γ-ZrH and ε-ZrH 2 , and the former follows the confirmed OR {0001} α //{111} δ/γ with α // δ/γ , while the latter's OR changed to {10 0} α //{121} ε with α // ε after HPT. The coexistence of δ-ZrH 1.5 and γ-ZrH or ε-ZrH 2 is observed, and the main corresponding OR is {111} δ //{111} γ with δ // γ , and {100} δ //{110} ε with δ // ε , respectively. The characterized microstructure and the measured lattice rotation results indicate that HPT delayed cracking in hydride and promoted deformation in parent grains. As the strain increases, the maintenance of hydride-matrix (H-M) coherent interfaces restricts further lattice rotation. HPT accelerates the hydride decomposition ascribed to the intensification of hydrogen diffusion under stress, and the hydride and the H-M interfaces act as priority sites for initiating microcracks. The sequence of HPT depends on the possibility of activated slip mode among grains. These findings contribute to developing the understanding of the HPT and hydrogen embrittlement.

Fretting corrosion behavior and microstructure evolution of hydrided zirconium alloy under gross slip regime in high temperature high pressure water environment

Understanding the fretting corrosion mechanism of zirconium alloy exposed to high temperature high pressure water

The Transformation of Fretting Corrosion Mechanism of Zirconium Alloy Tube Mating with 304 Stainless Steel in High Temperature High Pressure Water

Fretting corrosion running regime and damage mechanism evolution of zirconium alloy mated with Inconel 718 alloy in high temperature high pressure water environment

Evolution of Fretting Wear Behavior of Zirconium Alloy Cladding Tube under Gross Slip Regime in Simulated Primary Water of Pressurized Water Reactor

Fretting Wear Behaviour of Zr Alloy Cladding Tube under Partial Slip Regime with Different Duration in Simulated Primary Water of Pwr

Effect of coolant pH on the fretting corrosion behavior of zirconium alloy

Fretting Wear Behavior of Zr Alloy Cladding Tube Mated with Zr Alloy Dimple under Mixed Fretting Regime in Simulated Primary Water of PWR

Study on the fretting wear performance of oxide layer and Cr coating on zirconium alloy in high-temperature water

Fretting Wear Behavior of Zirconium Alloy in B-Li Water at 300 °C

Characterization and fretting wear behavior of zirconium alloy treated in high temperature water

Understanding the Microstructure Evolution of Ni-Based Superalloy Within Two Different Fretting Wear Regimes in High Temperature High Pressure Water

Exploring the Hydride-Slip Interaction in Zirconium Alloys

Effect of Micro-Arc Oxidation on Fretting Wear Behavior of Zirconium Alloy Exposed to High Temperature Water

Fretting Corrosion-Induced Microstructural Evolution of Alloy 690TT Tube in High Temperature Pressurised Water

Revealing the role of hydrogen content on the mechanical behavior and cracking mechanisms of Zircaloy-4 under strain

Effect of Normal Force on Fretting Wear Behavior of Zirconium Alloy Tube in Simulated Primary Water of PWR

In-situ EBSD analysis of hydride phase transformation and its effect on micromechanical behavior in Zircaloy-4 under uniaxial tensile loading

Wear and surface degradation of commercial ZTA femoral heads under boundary lubrication conditions

Investigation on the Failure Mechanistic Evolution of Fretting Corrosion of Alloy 690 with Increasing Cycles in High-Temperature Water

Modeling and tests on the damage and fracture behaviors of non-irradiated zirconium alloys with different hydrogen concentrations at RT and 350°C