Abstract:Zeolites with different structures (P1, sodalite, and X) were synthesized from coal fly ash by applying ultrasonically assisted hydrothermal and fusion–hydrothermal synthesis. Bimetallic catalysts, containing 5 wt.% Ni and 2.5 wt.% Cu, supported on the zeolites, were prepared by a post-synthesis incipient wetness impregnation method. The catalysts were characterized by X-ray powder diffraction (XRPD), N2 physisorption, transmission electron microscopy (TEM), Mössbauer and X-ray photoelectron spectroscopies (XPS), and H2–temperature-programmed reduction (H2-TPR) analyses. The XRPD results showed that crystalline Cu0 and NixCuy intermetallic nanoparticles were formed in the reduced catalysts. The presence of the intermetallic phase affected the reducibility of the nickel by shifting it to a lower temperature, as confirmed by the H2-TPR curves. Based on the Mössbauer spectroscopic results, it was established that the iron contamination of the coal fly ash zeolites (CFAZs) was distributed in ionic positions of the zeolite lattice and as a finely dispersed iron oxide phase on the external surface of the supports. The formation of the NiFe alloy, not detectable by XRPD, was also evidenced on the impregnated samples. The catalysts were studied in the upgrading of levulinic acid (LA), derived from lignocellulosic biomass, to γ-valerolactone (GVL), in a batch reactor under 30 bar H2 pressure at 150 and 200 °C, applying water as a solvent. The NiCu/SOD and NiCu/X catalysts showed total LA conversion and a high GVL yield (>75%) at a reaction temperature of 200 °C. It was found that the textural parameters of the catalysts have less influence on the catalytic activity, but rather the stable dispersion of metals during the reaction. The characterization of the spent catalyst found the rearrangement of the support structure. The high LA conversion and GVL yield can be attributed to the weak acidic character of the support and the moderate hydrogenation activity of the Ni-Cu sites with high dispersion.

Efficient Transformation of Levulinic Acid/esters to Γ-Valerolactone Via a Durable Catalyst with Simply Tunable Acid-Base Sites

Highly efficient Ni-Mn/SiO<sub>2</sub> catalyst for the selective hydrogenation of biomass-derived levulinic acid to -valerolactone under mild conditions

Highly Efficient Selective Hydrogenation of Levulinic Acid to Γ-Valerolactone over Cu–Re/TiO2 Bimetallic Catalysts

Low Loading of CoRe/TiO<sub>2</sub> for Efficient Hydrodeoxygenation of Levulinic Acid to -Valerolactone

Selective Production of gamma-Valerolactone and Valeric Acid in One-Pot Bifunctional Metal Catalysts

Sustainable Efficient Synthesis of Pyrrolidones from Levulinic Acid over Pd/C Catalyst

Catalytic Hydrogenation of Levulinic Acid to Gamma-Valerolactone over Ni/ZrO2

Conversion of levulinic acid and formic acid into γ-valerolactone over heterogeneous catalysts.

Selective Production of Γ-Valerolactone or 1,4-Pentanediol from Levulinic Acid/esters over Co-based Catalyst: Importance of the Synergy of Hydrogenation Sites and Acidic Sites

Copper-Based Catalysts With Tunable Acidic And Basic Sites For The Selective Conversion Of Levulinic Acid/Ester To Gamma-Valerolactone Or 1,4-Pentanediol

Zirconium Phosphate-Pillared Zeolite MCM-36 for Green Production of γ-Valerolactone from Levulinic Acid via Catalytic Transfer Hydrogenation

Surface-sealing encapsulation of phosphotungstic acid in microporous UiO-66 as bifunctional catalyst for transfer hydrogenation of levulinic acid to γ-valerolactone

Domino transformation of furfural to γ-valerolactone over SAPO-34 zeolite supported zirconium phosphate catalysts with tunable Lewis and Brønsted acid sites

SSZ-39 zeolite-based Ru catalysts for selective hydrogenation of levulinic acid to γ-valerolactone: Influence of synthesis method and zeolite acidity

Effective Conversion Of Biomass-Derived Ethyl Levulinate Into Gamma-Valerolactone Over Commercial Zeolite Supported Pt Catalysts

Selective Production of γ-Valerolactone from Biomass-Derived Levulinic acid over Ni/CMK-3 catalyst

The Formation of γ-Valerolactone from Renewable Levulinic Acid over Ni-Cu Fly Ash Zeolite Catalysts

Synthesis of Γ-Valerolactone from Ethyl Levulinate Hydrogenation and Ethyl 4-Hydroxypentanoate Lactonization over Supported Cu-Ni Bimetallic, Bifunctional Catalysts

Zinc-Incorporated Microporous Molecular Sieve for Mild Catalytic Hydrolysis of γ-Valerolactone: A New Selective Route for Biomass Conversion

Alkaline Modified Zr-loading on Nanosheet Zeolite Towards Production of γ-Valerolactone from Levulinic Acid Through Catalytic Transfer Hydrogenation

The solvent-free hydrogenation of butyl levulinate to γ-valerolactone and 1,4-pentanediol over skeletal Cu-Al-Zn catalyst