Achieving Strength-Ductility Synergy of Spark Plasma Sintered (cocrni)94al3ti3 Medium-Entropy Alloy Via Post-Sintering In-Situ Precipitation Treatment

Shifeng Luo,Nan Wang,Yan Wang,Xiang Li,Xiaogang Fang,Hongwei Zhou,Jieming Chen,Xinyu Yang,Jiuxing Zhang
DOI: https://doi.org/10.1016/j.jmrt.2024.09.090
2024-01-01
Abstract:The single-phase face-centered cubic medium-entropy alloys (MEAs) normally have coarse grains in as-cast state, which exhibit insufficient strength for engineering applications. Here, a superior tensile strength-ductility synergy in a fine grained (CoCrNi)(94)Al3Ti3 MEA hardened by nanoscale L1(2) precipitates was fabricated by spark plasma sintering (SPS) and post-sintering in-situ precipitation treatment. The SPSed MEAs have a fine grain size of similar to 5 mu m, and a high number density of L1(2) precipitates form after in-situ annealing within the SPS machine. A high tensile yield strength of 1141 MPa with an adequate elongation to fracture of 25.8% was achieved in (CoCrNi)(94)Al3Ti3 MEA after annealing at 700 degrees C for 4 h. Electron backscattered diffraction and transmission electron microscopy characterizations indicate that the superior mechanical properties mainly originate from fine grains and the coherent spherical L1(2) precipitates. The dislocation slips and stacking faults prevail in all SPSed MEAs during tensile deformation, while extra Lomer-Cottrell locks are observed in annealed MEAs. The deformation twinning is absent in these precipitation-hardened MEAs with a low stacking fault energy, which may be attributed to the fine grains and numerous nanoscale L1(2) precipitates. This study not only confirms the effectiveness of powder metallurgy when sintering and precipitation are combined in-situ during the SPS cycle, but also provide guidance for the microstructure regulation process and practical applications of SPSed HEAs/MEAs.
What problem does this paper attempt to address?