Tailoring recrystallization for optimum mechanical combination in Ni-rich medium-entropy alloy via simplified thermomechanical treatment

Nairan Wang,Yingjie Zhang,Li Cai,Qikun Huang,Zhenyuan Zhang,Wensheng Ma,Hao Wu,Yan Wang
DOI: https://doi.org/10.1016/j.jallcom.2024.174685
IF: 6.2
2024-05-07
Journal of Alloys and Compounds
Abstract:A simplified strategy is implemented to obtain the comprehensive strength-ductility synergy in the Ni 40 Fe 30 Co 20 Al 10 medium-entropy alloy (MEA) through one-pass cold-rolling (~80%) and annealing without pre-homogenization treatment. The MEA annealed at 800 °C (A800) consists of disordered face-centered-cubic (FCC) matrix (γ) with ordered FCC nanoscale precipitates (γ 1 ' and γ 2 '), displaying ultimate tensile strength (UTS) of 895 MPa coupled with uniform elongation (UE) of 29%. It is found the selective distribution behavior of nanoscale γ 1 ' and γ 2 ' as fully recrystallization (FR) precipitates within partially recrystallization (PR) and FR grains, exhibiting multiple nested-pattern heterostructure. The coarse-grained MEA annealed at 1200 °C (A1200) possesses a superior UE of ~70% and an UTS higher than that of the as-cast sample, which can be rationalized by the interweaved stacking faults/nanoscale deformation-twins and the continuously generated twin boundaries. Moreover, a new parameter k involving both UTS and UE is designed to unveil the salience of strength-ductility synergy. As compared with the reported MEAs within a similar yield strength range, A1200 MEA reveals the optimized k , and can be considered as an outstanding candidate for further thermomechanical treatment.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
What problem does this paper attempt to address?