Study on the Evolution of Multistage and Multiscale Ti-bearing Precipitation and Microstructure in Ultrahigh-Strength Titanium Microalloyed Weathering Steels

Feng Zhou,Lei Liu,Xiaohong Chu,Xiaolong Xu,Zhengrong Li,Chuangwei Wang,Zhengzhi Zhao

DOI: https://doi.org/10.1016/j.matchar.2024.114368

IF: 4.537

2024-01-01

Materials Characterization

Abstract:In this study, 900 MPa ultrahigh-strength weathering steels were successfully developed through thermomechanical controlled processing (TMCP). Advanced microstructure characterization, combined with precipitation thermodynamics and kinetics models, elucidated the evolution of Ti-bearing precipitation and microstructure. The results showed that coiling temperature (CT) significantly impacts phase fractions, grain boundary density, and misorientation angles, while both CT and finishing rolling temperature (FRT) influence grain sizes in acicular ferrite (AF) and granular bainite. The lower coiling temperature resulted in a higher dislocation density of the test steel, which provided more nucleation sites for AF and TiC, favoring a higher number of TiC particles and a higher proportion of AF. Above 1050 degrees C, the addition of nitrogen changed the shape of the precipitation kinetics curve, reduced the nucleation energy barrier of TiC, decreased the critical nucleation size, and improved the nucleation rate. Meanwhile, the addition of nitrogen accelerated the precipitation transformation of TiC, which promoted the formation of Ti(C, N). Furthermore, increasing the deformation stored energy (DSE) further accelerated the precipitation of Ti(C, N) and significantly increased the nucleation rate. The formation mechanism of large-size Ti(C, N) and the transformation mechanism of Ti(C, N) to TiC are revealed by precipitation thermodynamics and kinetics. The completion time of TiC precipitation on dislocations is shorter than that on grain boundaries, which results in the TiC on dislocations being prone to coarsening during prolonged coiling. These findings provide crucial insights for optimizing the industrial production of ultrahigh-strength titanium microalloyed weathering steels.