Preparing Gradient Microstructure to Achieve Enhanced Performance in GH4586 Superalloy: Experiments and Models

Ke Chen,Jiao Luo

DOI: https://doi.org/10.1016/j.msea.2024.147231

2024-01-01

Abstract:In this present study, a combined method of controlling strain deformation (CSD) and gradient-temperature heat treatment (GTHT) was adopted to prepare gradient microstructure in GH4586 superalloy. Consequently, it brought enhanced tensile strength from 1313.1 +/- 18.7 MPa at intermediate transition (IT) region to 1506.3 +/- 15.7 MPa at high-strain and low-temperature (HS-LT) region, presenting an improvement of 11.6%. And it also enhanced fracture toughness from 77.7 +/- 0.3 MPa center dot m(1/2) at IT region to 86.7 +/- 3.7 MPa center dot m(1/2) at low-strain and high-temperature (LS-HT) region, presenting an improvement of 14.7%. The formation of gradient microstructure along the longitudinal direction of CSD+GTHT-treated sample was thoroughly investigated from perspectives of precipitates distribution, activated slip systems and dislocations evolution. During CSD, the size and volume fraction of gamma ' precipitates decreased under the effect of strain-induced dissolution behavior. The activation of (1 11)[101] and (11 1)[011] slip systems dominated dislocation movement at each region and there retained increasing dislocation density due to more extensively activated slip systems at HS region. During GTHT, the high-density dislocations promoted recrystallization while the concentratedly distributed gamma ' precipitates obstructed movement of recrystallized front, leading to formation of heterogeneous structure with high-density grain boundaries and dislocations at HS-LT region. Finally, a model reflecting the effect of grain boundary strengthening, precipitation strengthening and dislocation strengthening on mechanical property of gradient microstructure was established and successfully applied to property prediction of GH4586 superalloy.