Abstract:In this present study, a combined method of controlling strain deformation (CSD) and gradient-temperature heat treatment (GTHT) was adopted to prepare gradient microstructure in GH4586 superalloy. Consequently, it brought enhanced tensile strength from 1313.1 +/- 18.7 MPa at intermediate transition (IT) region to 1506.3 +/- 15.7 MPa at high-strain and low-temperature (HS-LT) region, presenting an improvement of 11.6%. And it also enhanced fracture toughness from 77.7 +/- 0.3 MPa center dot m(1/2) at IT region to 86.7 +/- 3.7 MPa center dot m(1/2) at low-strain and high-temperature (LS-HT) region, presenting an improvement of 14.7%. The formation of gradient microstructure along the longitudinal direction of CSD+GTHT-treated sample was thoroughly investigated from perspectives of precipitates distribution, activated slip systems and dislocations evolution. During CSD, the size and volume fraction of gamma ' precipitates decreased under the effect of strain-induced dissolution behavior. The activation of (1 11)[101] and (11 1)[011] slip systems dominated dislocation movement at each region and there retained increasing dislocation density due to more extensively activated slip systems at HS region. During GTHT, the high-density dislocations promoted recrystallization while the concentratedly distributed gamma ' precipitates obstructed movement of recrystallized front, leading to formation of heterogeneous structure with high-density grain boundaries and dislocations at HS-LT region. Finally, a model reflecting the effect of grain boundary strengthening, precipitation strengthening and dislocation strengthening on mechanical property of gradient microstructure was established and successfully applied to property prediction of GH4586 superalloy.

Effects of Post-Heat Treatment and Carbide Precipitates on Strength-Ductility Balance of GH3536 Superalloy Prepared by Selective Laser Melting

Mechanical Properties and Fracture Behavior of Laser Powder-Bed-Fused GH3536 Superalloy

In-situ Study of Microstructure and Mechanical Properties of GH3536 Alloy Manufactured by Selective Laser Melting at 750 °C

Effect of Heat Treatment on Microstructure and Residual Stress of GH3536 Superalloy Fabricated by Selective Laser Melting

Effect of Heat Treatment on Microstructure and High Temperature Tensile Mechanical Properties of Selective-Laser-Melted GH3230 Superalloy

Preparing Gradient Microstructure to Achieve Enhanced Performance in GH4586 Superalloy: Experiments and Models

Effect of Post Treatment on the Microstructure and Properties of the GH3536 Alloy Formed by Additive Manufacturing

Influence of Heat Treatment Temperature on Grain Structures and Properties of a Ni-based Superalloy Fabricated Via Selective Laser Melting

GH3536 Superalloy Prepared by Selective Laser Melting: Microstructure and Properties

Experimental Characterization and Strengthening Mechanism of Process-Structure-property of Selective Laser Melted 316 L

Effect of Heat Treatment on Microstructure and Mechanical Properties of a Selective Laser Melting Processed Ni-Based Superalloy GTD222

Effects of Heat Treatments on the Microstructure and Tensile Properties of IN738 Superalloy with High Carbon Content Fabricated Via Laser Powder Bed Fusion

The effect of subsequent heating treatment on the microstructure and mechanical properties of additive manufactured Hastelloy X alloy

Investigating the Anisotropic Behavior and High-Temperature Mechanical Properties of GH4251 Nickel-Based Superalloy Prepared by Selective Laser Melting and Post Heat Treatment

Influence of Various Heat Treatments on Microstructures and Mechanical Properties of GH4099 Superalloy Produced by Laser Powder Bed Fusion

Effect of ultrasonic shot peening on microstructure and mechanical properties of GH3230 superalloy during selective laser melt solution heat treatment

Effect of Hot Isostatic Pressing Temperature on Microcrack,Microstructure and Mechanical Properties of GH3536 Nickel-based Superalloy Fabricated by Selective Laser Melting

Effect of Heat Treatment on Microstructure and Mechanical Properties of a Selective Laser Melted Cu–15Ni–8Sn Alloy

Strength-plasticity transition mechanism after the solution treatment of GH3230 superalloy fabricated via laser powder bed fusion

Effect of Heat Treatment on the Microstructural Evolution of a Precipitation-Hardened Superalloy Produced by Selective Laser Melting

Effect of Post Processing Heat Treatment Routes on Microstructure and Mechanical Property Evolution of Haynes 282 Ni-Based Superalloy Fabricated with Selective Laser Melting (SLM)