Study on Low Cycle Fatigue Properties of Cr-Mo Steel in 50 MPa Gaseous Hydrogen

Jinyang Zheng,Jiangchuan Hu,Kai Ma,Yiming Zhao,Ruiming Zhang,Chaohua Gu,Zhengli Hua

DOI: https://doi.org/10.1016/j.ijhydene.2024.08.270

IF: 7.2

2024-01-01

International Journal of Hydrogen Energy

Abstract:At present, a lack of fatigue design curves for Cr-Mo steel in high-pressure gaseous hydrogen worldwide impedes the use of the design fatigue curve (S-N curve) evaluation for vessel fatigue design, necessitating reliance on fracture mechanics methods related to the initial crack size. In this study, strain-controlled fatigue tests with a strain ratio of -1 were carried out in 50 MPa gaseous hydrogen to study the low cycle fatigue properties of Cr-Mo steel. Results indicate that hydrogen reduces the fatigue life of 4130X under high strain amplitudes. Under 0.5 % strain amplitude, different from characteristics of ductile fracture in air, the fracture in 50 MPa gaseous hydrogen showed quasi-cleavage and intergranular fracture characteristics. Based on the test results, the S-N curve in 50 MPa gaseous hydrogen was obtained with fatigue life safety factor 20 and stress amplitude safety factor 2. The SN curve in 50 MPa gaseous hydrogen is under the curve in KD-320.2 M of the 2023 ASME Boiler & Pressure Vessel Code VIII-3, which does not consider the effect of hydrogen, when the number of cycles to failure is less than 1x106. This indicates that the fatigue life calculated by the S-N curve in KD-320.2 M cannot ensure that 50 MPa high-pressure hydrogen storage vessels avoid fatigue failure under high stress amplitudes.