The dependence of fatigue property on applied stress in X80 pipeline steel notched specimens in hydrogen gas environment
Zhongxiang Lin,Meng Wang,Guoming Sun,Jinsheng Wang,Fanfan Zhang,Liangliang Li,Meng Zhang,Liangliang Huang,Kaiyu Zhang,Lin Zhang,Jinyang Zheng
DOI: https://doi.org/10.1016/j.ijfatigue.2024.108222
IF: 5.489
2024-06-01
International Journal of Fatigue
Abstract:The effect of applied stress on the fatigue property in X80 pipeline steel notched specimens was investigated in hydrogen gas environment. In hydrogen gas, a turning point (ΔKT) was observed in the curve of the fatigue crack growth (FCG) rate, and the fatigue crack propagation was significantly accelerated after the stress intensity factor (ΔK) exceeded ΔKT. The fracture of the notched specimen undergoes two stages: the first stage was the initiation and slow propagation of cracks at the root of the notch, which was similar in hydrogen and nitrogen gases; The second stage was the appearance of the concave boundary between the ductile striations and the quasi-cleavage (QC) features on the fracture surface, which only occurred in hydrogen gas environment. According to the fatigue life test results, the decrease in fatigue life was due to hydrogen enhancing the FCG rate in the second stage when the applied stress was enormous; the decrease in fatigue life was caused by hydrogen promoting the initiation of fatigue cracks when the applied stress was small.
materials science, multidisciplinary,engineering, mechanical