Systematic Analysis of Distinct Flow Characteristics and Underlying Microstructural Evolution Mechanisms of a Novel Fine-Grained P/M Nickel-Based Superalloy During Isothermal Compression
Hongning Wen,Junsong Jin,Xuefeng Tang,Xinyun Wang,Heyang Yang,Yiding Zhang,Lei Deng,Pan Gong,Qingsong Wei,Yingjie He,Jianzheng Guo
DOI: https://doi.org/10.1016/j.jmst.2023.03.042
2023-01-01
Journal of Material Science and Technology
Abstract:Isothermal forging (IF) is an effective method for forming difficult-to-deform materials like P/M superalloys. Understanding the isothermal compression microstructural evolution mechanism of a novel P/M superalloy provides the basis for its optimized IF planning. In this study, the isothermal compression tests of a novel fine-grained P/M nickel-based superalloy were carried out at 10 0 0-1150 degrees C with strain rates of 0.001-0.01 s -1 . The results indicated that the alloy exhibits three distinct flow characteristics: continuous softening after reaching the peak stress, near-steady superplastic flow, and discontinuous hardening, corresponding to different strain rate sensitivity exponent ( m ) values. Varied microstructural evolution mechanisms, including grain boundary sliding (GBS), dynamic recrystallization (DRX), and grain growth, are dominated in different m -value domains. Meanwhile, different roles of primary gamma ' play in microstructural evolution were clarified. A moderate fraction of primary gamma ' with 8.5%-14.2% can well coordinate the GBS and hinder excessive grain growth at a high m value domain ( m > 0.4). When 0.2 < m < 0.4, the role of the primary gamma ' is changed to promote dislocation accumulation, accelerating the nucleation of DRXed grains. As the primary gamma ' is dissolved at 1150 degrees C, obvious grain growth was observed after compression. Work hardening effect by overgrown grains competed with DRX softening results in the discontinuous rising stress. (c) 2023 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.