Orientational growth behavior and mechanism of delta (δ) phase precipitation in cold-rolled Inconel 718 alloy during heat treatment
Neng-yong Ye,Guang-liang Zhang,Tian-yue Huang,Ming Cheng,Shi-hong Zhang,Lei Wang
DOI: https://doi.org/10.1007/s42243-023-00955-z
2023-04-13
Journal of Iron and Steel Research International
Abstract:Due to the important role of δ phase’s quantity and morphology in the mechanical and fatigue properties of Inconel 718 alloy and its components, it is necessary to renew insights into the effect of cold deformation on the δ phase precipitation, especially on the morphology evolution. Therefore, the nucleation and growth behavior of δ phase in cold-rolled Inconel 718 alloy during aging were investigated. The results show that the precipitation rate and volume fraction of δ phase increase with increasing the cold rolling reduction from 10% to 50%. The volume fraction of δ phase reaches equilibrium after 5 h, remaining at 5.98%, 6.52%, and 6.79% under different rolling reductions (10%, 30%, and 50%), respectively. The nucleation of δ phase mainly occurs on different sites (grain boundaries, new twin boundaries and old twin boundaries) under 10% rolling reduction, while δ phase mainly nucleates on the new grain boundaries of static recrystallization due to 50% rolling reduction. And the growth of δ phase undergoes a process of alternate orientation growth from spherical (nucleation) → short rod (longitudinal orientation growth) → short rod (radial orientation growth) → dynamic equilibrium. Under 10% rolling reduction, δ phase tends to grow into the matrix, while under 50% rolling reduction, the orientation grows faster and is easily affected by the grain boundary curvature.
metallurgy & metallurgical engineering