Wetting Kinetics of Molten Carbonate on Carbon
Yanpeng Dou,Peng Li,Kaifa Du,Peilin Wang,Huayi Yin,Dihua Wang
DOI: https://doi.org/10.1021/acs.langmuir.1c01886
IF: 3.9
2021-08-26
Langmuir
Abstract:The wettability of molten carbonate on carbon determines the electrochemical performances of high-temperature direct carbon fuel cells (DCFCs). However, a universal method to measure the high-temperature wettability of molten carbonate is absent and the wetting kinetics is not well understood. Herein, we develop a dispensed drop (DD) method to measure the wetting kinetics of molten carbonate (Li2CO3–Na2CO3–K2CO3, 43.5:31.5:25.0, molar ratio) on the carbon substrate at 450–750 °C under controlled atmospheres (100%Ar, 100%CO2, and 1%O2–99%N2). The measured contact angles under different conditions reveal that increasing the O2– concentration in the gas–liquid–solid (GLS) interface decreases the contact angle. In addition, elevating the temperature, introducing O2 in the gas atmosphere, or pretreating the carbon substrate can enhance the wetting kinetics of molten carbonates. The molten carbonate completely wets the carbon substrate in 150 min in Ar gas atmosphere and in 30 min in 1%O2–99%N2 gas atmosphere at 600 °C. Further, it takes only 30 min to completely wet the pretreated carbon substrate in Ar atmosphere at 600 °C. Overall, this paper offers the DD method to study the wettability of molten carbonate on the carbon substrate, which is helpful to understand the underlying wetting mechanism and engineer the electrode design for DCFCs.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acs.langmuir.1c01886.Profiles of the drop base radius R and contact angle θ as a function of time of MTC droplet on carbon substrate at different temperatures (450–750 °C, Figures S1–S3, Tables S1–S3 in Ar gas atmosphere), in various gas atmospheres (pure CO2 and 1%O2–99%N2, Figures S4 and S5, Tables S4 and S5, at 600 °C), on pretreated carbon (Figure S6, Table S7, in Ar gas atmosphere at 600 °C), MTC-Li2O (Figure S7, Table S8, on pristine carbon in Ar gas atmosphere at 600 °C), and in pure CO2 gas atmosphere (450 and 750 °C, Figures S8–S11, Tables S9 and S10, on carbon); atomic ratio of C and O on carbon measured by EDS and XPS on pristine carbon and pretreated carbon, respectively (Table S6); calculation of the basicity of molten MTC; and Kd, viscosity, and liquid–gas surface tensions γlg of MTC at different temperatures (Tables S11 and S12, Figure S12) (PDF)This article has not yet been cited by other publications.
chemistry, multidisciplinary, physical,materials science