Formation, microstructure, and mechanical properties of oscillating laser-welded joints of 8-mm 304 stainless steel
Peikang Tao,Chunming Wang,Gaoyang Mi,Yu Huang,Xiong Zhang
DOI: https://doi.org/10.1007/s00170-023-12868-y
IF: 3.563
2023-12-24
The International Journal of Advanced Manufacturing Technology
Abstract:Oscillating laser could improve the welding stability and eliminate defects compared to the conventional laser welding. In this paper, the butt joints of 304 stainless steel with 8 mm thickness were made by oscillation laser welding. The relationship between the oscillating parameters, energy distribution, flow dynamics, formation, microstructure, and mechanical properties were established. The results showed that the oscillation amplitude largely affected energy density and size of the melt pool, while oscillation frequency had a notable effect on trajectory line energy and stability of the keyhole. Defects including collapse, spatters, and pores emerged when inappropriate oscillation parameters were used. Increased amplitude (0.9 to 1.5 mm) to reduce the spatter generation and lower frequency (300 to 100 Hz) to reduce the porosity of the weld (2.1 to 0.2%). Differences of the microstructure of the weld zone at different oscillation parameters were small owing to homogenization of temperature field and similarity of the thermal cycling profiles which leaded to a consistent process of structure evolution. Unequilibrium solidification processes in the molten pool increase dislocation density in the weld zone, resulted in welded joint with higher yield strengths than the base metal. On the other hand, tensile strength of the joint was little lower than that of base metal due to porosity defects. Under oscillation parameters of 1.5 mm–100 Hz, tensile strength of the welded joints reached 99.7% of base metal, and yield strength increased by 8.7% compared to the base material, indicating an acceptable welding quality.
engineering, manufacturing,automation & control systems