Microstructure evolution and fracture behavior of rotating laser welded-brazed 6061 aluminum alloys/304 SS dissimilar joint
Jia Xie,Chuang Cai,Bingbing Zhang,Jie Yu,Yonghong Liu,Hui Chen
DOI: https://doi.org/10.1016/j.matchar.2022.112543
IF: 4.537
2022-12-11
Materials Characterization
Abstract:In the study, rotating laser welding-brazing technology was developed to weld aluminum alloys and stainless steel. The influence of rotating laser on microstructure evolution and fracture behavior of joints were investigated. Only τ 5 -(Fe, Ni) 1.8 Al 7.2 Si with a thickness of 3.5 μm was formed in the rotating laser welded-brazed interface layer. The phases generated in the laser welded-brazed interface were τ 5 -(Fe, Ni) 1.8 Al 7.2 Si, θ-(Fe, Ni)(Al, Si) 3 , FeAl 2 , and (Fe, Ni) 3 Al. Line load of rotating laser welded-brazed joint was about 30.1% higher than that of laser welded-brazed joint. Fracture of rotating laser welded-brazed joint occurred in the weld rather than along intermetallic compounds layer. The formation of intermetallic compounds was inhibited and thickness of intermetallic compounds layer decreased due to lower peak temperature on rotating laser welded-brazed interface. The peak temperature of interface and diffusion coefficient of Fe atoms decreased due to optimized temperature distribution caused by rotating laser. The line load of rotating laser welded-brazed joint increased obviously as interplanar spacing mismatch rates of τ 5 -(Fe, Ni) 1.8 Al 7.2 Si/weld and τ 5 -(Fe, Ni) 1.8 Al 7.2 Si/steel were significantly lower than that of τ 5 -(Fe, Ni) 1.8 Al 7.2 Si/θ-(Fe, Ni)(Al, Si) 3 .
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing