Investigation of Supercritical CO2 Corrosion Behavior of X80 Carbon Steel in Pipelines: an in Situ Experimental and DFT Study

Xiaodan Wang,Pu Yang,Ruidong Li,Guohu Tong,Jukai Chen,Yueshe Wang

DOI: https://doi.org/10.1016/j.supflu.2024.106371

2024-01-01

Abstract:The electrochemical corrosion behavior of X80 carbon steel was investigated in a supercritical CO2 2 (sCO2) 2 ) environment at 60 degree celsius and 9 MPa, by in-situ experiments and density functional theory (DFT) calculations, revealing the corrosion mechanism. For in situ electrochemical measurements, two novel CO2-rich 2-rich and H2O-rich 2 O-rich cells were developed to replace the traditional three-electrode cell. Electrochemical impedance spectroscopy revealed distinct differences in the corrosion behavior between CO2-rich 2-rich and H2O-rich 2 O-rich environments during the later stages of testing. In H2O-rich 2 O-rich environments, as corrosion time increased, the corrosion product layer gradually changed from porous to dense, eventually forming a protective layer. In CO2-rich 2-rich environments, corrosion occurs mainly in areas where water condenses to form FeCO3. 3 . Simultaneously, microscopic calculations provided evidence for the three-step sCO2 2 hydrolysis mechanism and the formation of FeCO3 3 products.