Component Design and Stable SESAM Mode-Locking of the Disorder Middle Entropy Yb:CaSrBaF6 Single Crystal

Wudi Wang,Qingguo Wang,Chenbo Zhang,Jian Liu,Zhen Zhang,Yuqian Zu,Qi Yang,Qiancheng Fang,Yanyan Xue,Bo Liu,Dongzhen Li,Xiaodong Xu,Huili Tang,Liangbi Su,Jun Xu

DOI: https://doi.org/10.1364/oe.504864

IF: 3.8

2024-01-01

Optics Express

Abstract:To the best of our knowledge, this is the first report on continuous and passively mode-locked operation of the multi-component fluoride CaSrBaF6 6 crystal. A novel disorder laser material, Yb:CaSrBaF6 6 (Ca 0.33 Sr 0.33 Ba 0.33 F 2 ) of multi-component middle entropy crystal was designed and grown by temperature gradient technique (TGT) for the first time. X-ray diffraction (XRD) and X-ray fluorescence (XRF) analysis of Yb:CaSrBaF6 6 crystal reveals that Ca2+, 2 + , Sr2+, 2 + , and Ba2+ 2 + of near equal atomic ratio (1:1:1) have formed a homogeneous single-phased fluorite solid solution. The first principle calculation further shows that Ca2+, 2 + , Sr2+, 2 + , Ba2+ 2 + ions tend to be evenly distributed in the matrix crystal. The total formation energy is the lowest-547.17 ev and the structure is also the most stable at this time. The spectral properties of the crystal are systematically characterized. The emission cross section of 2F5/2 -> 2F7/2 F 5 / 2 -> 2 F 7 / 2 transition at 1040 nm is 0.62 x 10-20 - 20 cm2 2 with the larger full width at half maximum (FWHM) of 60.5 nm. The evenly disordered distribution of various cations and lattice distortion effect leads to the more diverse local structure and the diversity of luminescence, which can cause non-uniform broadening of the spectrum. Meanwhile, the Yb:CaSrBaF6 6 crystal generated a continuous wave (CW) output power of 1.128 W, corresponding to a slope efficiency of 32% and an optical-to-optical conversion efficiency of 28.7% at 1055.4 nm. By implementing a semiconductor saturable absorber mirror (SESAM) for stable mode-locked laser operation, when the absorbed pump power reached 3.79 W, the laser ran into continuous wave mode-locking (CWML) regime, the maximum average output power of 123 mW was generated and the pulse duration of 89 ps was achieved at a pulse repetition rate of 54.6 MHz, with a pulse energy of 2.25 nJ and a pulse peak power of 25 W. Better laser performance could be expected after optimizing pump core diameter and elimination of dispersion. All results show that Yb:CaSrBaF6 6 crystal is regarded as a what we believe to be novel laser materials, which also provide a reference for the development of disordered material and other rare earth ions doping.