Abstract:Yb:CALYGLO crystals with a dopant concentration of 5 at.% were successfully grown using the Czochralski method. The crystal samples were extensively studied to analyze their structure, room temperature and low temperature spectra, and laser properties. The highest absorption cross-section at 977 nm was calculated to be 1.83 × 10−20 cm2 for σ polarization and 5.32 × 10−20 cm2 for π polarization. Similarly, the emission cross-section was determined to be 1.38 × 10−20 cm2 at 980 nm for σ polarization and 2.28 × 10−20 cm2 at 981 nm for π polarization, with a full width at half maximum (FWHM) of 50.3 nm and 89.5 nm, respectively. The fluorescence lifetime of the 5 at.% Yb:CALYGLO crystal at 2F5/2 was measured to be 1.10 ms. Additionally, gain cross-sections were calculated for different β values. In the continuous laser experiment, the crystal demonstrated a laser output of 20.15 W at 1057 nm, with a slope efficiency of 53.3%. These experimental findings indicate that the lattice of Y3+ in the crystal is partially replaced by Lu3+ and Gd3+, resulting in a broader spectrum. Consequently, this crystal shows promising potential as a gain medium for ultrashort pulse laser crystals.

Continuous-wave and Passively Mode-Locked Operation of Yb:Ca3Gd2(BO3)4 Laser

Growth, spectroscopy and SESAM mode-locking of a "mixed" Yb:Ca(Gd,Y)AlO4 disordered crystal

Spectroscopy and Kerr-lens mode-locked operation of Yb:GdScO3 crystal

Continuous-wave and SESAM mode-locked operation of a Yb:YSr3(PO4)3 laser

Free-running Performance of Yb0.14:Y0.77

Anisotropic Lasing Properties in the 1059−1086 Nm Range of Yb:YCa4O(BO3)3 Crystal

Spectroscopic, Thermal, and Laser Properties of Yb:CaNb $_{2}$ O $_{6}$ Crystal

SESAM mode-locked Yb:GdScO3 laser

Quasi-three-level laser pumped Yb:GdCOB tunable laser from 1030 to 1036 nm

High-power Dual-Polarization Laser Operation of Yb:LaCa4O(BO3)

430mw Diode-Pumped Yb : Gdcob Laser And Its Thermal Effect

Kerr-lens mode-locking of an Yb:CLNGG laser

A potential ultrafast pulse laser crystal with disordered melilite structure: Yb3+: CaLaGa3O7

Advances of Yb:CALGO Laser Crystals

Performance of an Yb:LaCa4O(BO3)3 Crystal Laser at 1.03–1.04 Μm Passively Q-switched with 2D MoTe2 Saturable Absorber

Continuous-wave laser performance of 10 at% Yb:YSAG transparent ceramics

Spectroscopy and Kerr-lens mode-locked operation of Yb:GdScO_3 crystal

Diode-pumped Passively Mode-Locked Nd:GYSGG Laser at 1061 Nm with Periodically Poled LiNbO3 Nonlinear Mirror

Passively Q-switched Laser Action of Yb:LaCa4O(BO3)3 Crystal

Growth and Characterization of Yb: CALYGLO Crystal for Ultrashort Pulse Laser Applications

Quasi-three-level Yb:CN Laser at 978 nm and the Second-harmonic Generation