Abstract:Wood, a flammable material, poses safety risks due to heat and smoke release during combustion and is a huge safety hazard. The current approach involves impregnating water-soluble inorganic flame retardants into wood. However, these retardants are susceptible to leaching, negatively impacting the aesthetic appearance and flame retardancy of wood. Herein, a liquid mix of ammonium dihydrogen phosphate, boric acid, and magnesium chloride was vacuum-pressure impregnated into wood. Subsequent concentration and drying produced composite salt particles (named as P-B-Mg). The wood was immersed in sodium silicate solutions of different concentrations. Mg2+ leached from P-B-Mg rapidly combined with SiO32- to precipitate an MgSiO3 layer on the particle surfaces. This in-situ synthesis resulted in P-B-Mg@MgSiO3 hybrid flame retardant with core-shell structure within wood cells. The modified wood displayed superior performance, achieving non-combustible level in limiting oxygen index test and remaining self-extinguishing even after continuous exposure to open flame at 1100 degrees C for 205 s. Compared with that of untreated wood, the total heat release and total smoke production of the P-B-Mg@40%MgSiO3-modified wood decreased by 94.7 and 86.5 %, respectively. Residual char and pyrolysis analysis showed that the flame retarded process of modified wood involved gas, liquid and solid phase synergy effects. Meanwhile, the modified wood exhibited excellent resistance to leaching, durable flame retardancy, smoke suppression after 14-d water immersion cycles. Furthermore, it displayed good anti-degradation properties with pH value close to that of untreated wood. Thus, the modified wood possesses stable material properties suitable for long-term use in both indoor and outdoor applications.

Producing Sustainable Flame-Retardant Room Temperature Phosphorescent Materials from Natural Wood Assisted by Borax

Sustainable Afterglow Materials from Lignin Inspired by Wood Phosphorescence

Room Temperature Phosphorescence from Natural Wood Activated by External Chloride Anion Treatment

Structural materials with afterglow room temperature phosphorescence activated by lignin oxidation

Producing Sustainable Room Temperature Phosphorescent Materials Using Natural Wood and Sucrose

Synthesis of vanillin-based flame retardant epoxy coating on wood surface

Producing a Room Temperature Phosphorescent Film from Natural Wood Using a Top‐Down Approach

Room-temperature phosphorescence from bamboo fibers and designed materials

Highly transparent cellulose-based phosphorescent materials with tunable afterglow colors and white emission

A Facile and Green Strategy to Obtain Organic Room-Temperature Phosphorescence from Natural Lignin

In-Situ Synthesized Phosphorus–Boron–Magnesium Hybrid Flame Retardants with Core-Shell Structures in Wood Microstructures: an Effective Strategy for Realizing Durable Fire Retardancy, Smoke Suppression, and Anti-Degradation

Colorful Room‐Temperature Phosphorescence Including White Afterglow from Mechanical Robust Transparent Wood for Time Delay Lighting

A Top-Down Approach to the Fabrication of Flame-Retardant Wood Aerogel with In Situ-Synthesized Borax and Zinc Borate

Abnormal room temperature phosphorescence of purely organic boron-containing compounds: the relationship between the emissive behaviorand the molecular packing, and the potential related applications.

Photoactivated room temperature phosphorescence from lignin

Synthesis of bio-based flame-retardant epoxy co-curing agent and application in wood surface coating

Acid-base Synergistic Flame Retardant Wood Pulp Paper with High Thermal Stability.

Flame Retardancy of Densified Wood Modified by Bio-Material Based Flame Retardant

Highly Flame-Retardant and Low Heat/Smoke-Release Wood Materials: Fabrication and Properties

Producing long afterglow by cellulose confinement effect: A wood-inspired design for sustainable phosphorescent materials

Synergistic Flame-Retardant and Smoke Suppression Effects of Zinc Borate in Transparent Intumescent Fire-Retardant Coatings Applied on Wood Substrates