Abstract:In ceramic/metal brazing, high residual stress usually causes fracture in the ceramic substrates. Therefore, composite fillers consisting of ductile matrix featuring low yield strength and elastic modulus, as well as reinforcements featuring low coefficient of thermal expansion (CTE), are employed. However, for AgCuTi-base composite fillers, the reinforcements are likely to weaken the deformability of brazing seams (BS), i.e. increase the elastic modulus and yield stress of BS. To address this issue, we developed a new AgCu-base composite filler with "hedgehog-like" reinforcement clusters. Herein, AgCu + NbB2 composite filler was used to braze ZrB2-SiC and TC4-TiBw, wherein ductile Ag(s,s) and Cu(s,s) dominated BS, thereby ensuring high deformability; in addition, a NbB layer along with limited TiB whiskers was formed at the NbB2/brazes interface with the orientation relationship of (-11-1)NbB//(0-1-1)TiB and [-314]NbB//[12-2]TiB, resulting in "hedgehog-like" reinforcement clusters. This structure exhibited the following advantages: (i) crystallographic misfit at the interface of reinforcement clusters/brazes and the controlled formation of TiB whiskers minimised the conventional fine grain strengthening and dispersion strengthening effects of BS; (ii) isolated reinforcement clusters decelerated the increase in the elastic property of BS; (iii) "hedgehog-like" structure absorbed fracture energy by deflecting cracks; and (iv) the formation of brittle compounds could be avoided. In other words, the designed reinforcement clusters reduced the deformability expense and compensated for the mechanical-resistance of BS. Therefore, the maximum joint strength was obtained with 2 wt% NbB2, which increased the shear strength of the joint six times compared to that with 0 wt% NbB2. For the joints failing inside ceramic substrates, (i) the key factor for limiting joint strength was the residual stress inside ceramics and (ii) the remission of the trade-off between thermal expansion mismatch and deformability expense contributed to relaxing residual stress, thereby confirming the reliability of our design.

Strengthening Ti3SiC2/Cu Brazed Joint Assisted with Cold Spray Additive Manufacturing: Lower Brazing Temperature Through Interdiffusion and Graded Reinforcement for Stress Relaxation

Improvement for Ti3SiC2/Cu Joint Brazed Using Composite Fillers with Abnormal Expansion Ceramic Particulates

Improvement for Ti 3 SiC 2 /Cu joint brazed using composite fillers with abnormal expansion ceramic particulates

Achieving ultrafine grain strengthening C f /SiC-GH3536 joints brazed with Cu-Ti-WC composite interlayer via cold spray additive manufacturing

Achieving Ultrafine Grain Strengthening Cf/SiC-GH3536 Joints Brazed with Cu-Ti-WC Composite Interlayer Via Cold Spray Additive Manufacturing

Solid-state Transformation Composite Filler: A New Strategy to Strengthen Ceramic/metal Joint

Achieving Ultrafine Grain Strengthening Cf/SiC-GH3536 F /Sic-Gh3536 Joints Brazed with Cu-Ti-WC Composite Interlayer Via Cold Spray Additive Manufacturing

Effects of Interfacial Reaction and Atomic Diffusion on the Mechanical Property of Ti 3 SiC 2 Ceramic to Cu Brazing Joints

Brazing ZrO2 Ceramic and TC4 Alloy by Novel WB Reinforced Ag-Cu Composite Filler: Microstructure and Properties

Design of composite filler with hedgehog-like reinforcement clusters for effective stress relief in ceramic/metal joints

Brazing of ZrB 2 –SiC–C ceramic and GH99 superalloy to form reticular seam with low residual stress

In Situ Consume Excessive Ti Element and Form Fine Ti Based Compounds As Reinforcements for Strengthening C/C-Tc4 Joints

Design and Preparation of High-Content Sc2W3O12 Dispersed Interlayer: Alleviating the High Residual Stress of Cf/SiC and GH3536 Joint

Effect of AgCu/Cu Foam/agcu Composite Filler on Microstructure and Mechanical Properties of ZrB2-SiC/Inconel 600 Alloy Brazed Joints

Unveiling Solid-State Transformation Toughening Mechanism of Yttria Stabilized Zirconia on Brazed Joint by In-Situ Observation

Reliable brazing of SiBCN ceramic and TC4 alloy using AgCuTi filler with the assist of laser melting deposited FGM layers

A Novel Method to Relieve Residual Stress in Dissimilar Brazed Joint Via Micro-Scale Additive Manufacturing

C/SiC composite-Ti6Al4V joints brazed with negative thermal expansion ZrP2WO12 nanoparticle reinforced AgCu alloy

Microstructure and Mechanical Properties of the SiC/Nb Joint Brazed Using AgCuTi + B4C Composite Filler Metal

Investigating the effect of WC reinforcements in Cu Ti composite filler on the microstructural evolution and mechanical characteristics in brazing C f /SiC and GH3536

Compression Brazing of SiCp/Al Composite Using a Semisolid Zn-Al-Cu Filler Metal Based on the Strain-Induced Melt Activation Process