Abstract:NiCoCrAlY+(6–8wt%)Y2O3 stabilized ZrO2(YSZ) two-layer thermal barrier coatings (TBCs) were deposited by electron beam physical vapor deposition on Ni3Al or Ni-base superalloy and their high temperature fatigue behavior was investigated experimentally and computationally. It has been found that the pre-treatment of the bond coat has greatly improved the thermal cyclic lifetime of TBCs with respect to those without pre-treatment. The lifetime is limited by the existence of interface between bond coat and top coat, and smoothing the interface can also improve the thermal cyclic lifetime. When the roughness of the interface changed from 3.76 to 0.82μm, testing lifetime increased from about 500 (1000 cycles) to 700h (1400 cycles), and the adhesive strength of the interface increased from 3.5 to 4.7MPam1/2 estimated from the result of surface Rock-well hardness testing. Cracks occurred in the thermally grown oxide (TGO) layer are considered to be the main reason for the failure of two-layer TBCs. It has been found that with pre-oxide layer thickness increasing from 1.0 to 3.0μm, the growth rate of TGO increased during thermal cyclic testing and the thermal cyclic lifetime of TBCs decreased from 730 to 450h. The lower lifetime was caused by the co-action of larger internal stress resulted from thicker TGO layer and the fatigue of the TGO layer. Finite element method (FEM) analysis showed that large tensile stress was introduced at the beginning of rapid cooling process, resulting in the spallation of top coat from bond coat. Ab initio calculation was carried out to evaluate the binding energy of the interface of bond coat and ceramic top coat, and FEM models were used to investigate stress and strain states in TBCs during thermal shock process as a function of cooling rate. The results showed that ZrO2/Ni interface exhibits nonmetallic properties, and that the chemical bonding in ZrO2/Ni is covalent–ionic in nature. The calculation of binding energies between both Ni and O and Zr and O indicates that the binding energy of Ni and O is larger than that of Zr and O, which is helpful to investigate the failure mechanism of thermal barrier coatings.

Foreign Object Damage Behavior and Failure Mechanism of Al2O3-modified TBCs Prepared by PS-PVD

Different Growth Mechanisms of Alumina on the Surface of NiPtAl and MCrAlY Bondcoatings in EB-PVD TBC System

Enhancing the performances of EB-PVD TBCs via overlayer Al-modification

Preparation and Solid Particle Erosion Behaviors of Plasma-Sprayed and Laser-Remelted ZrO2-7wt.%Y2O3 Thermal Barrier Coatings

Preparation and High Temperature Oxidation Resistance of Thermal Barrier Coatings on Ti-Al Alloys by EB-PVD

Influence of interface morphology on erosion failure of thermal barrier coatings

Experimental and computational study on hot fatigue process of thermal barrier coatings by EB-PVD

Al2O3-modified PS-PVD 7YSZ thermal barrier coatings for advanced gas-turbine engines

PS–PVD Alumina Overlayer on Thermal Barrier Coatings Against CMAS Attack

Experimental Investigation and Theoretical Prediction on the Erosion Resistance of the Y0.5Gd0.5TaO4 Thermal Barrier Coatings at Room Temperature

Failure Behavior Study of EB-PVD TBCs under Salt Spray Corrosion and Thermal Shock Cycles

Corrosion Resistance of the Al2O3+ZrO2 Thermal Barrier Coatings on Stainless Steel Substrates

Failure Mechanism of EB-PVD Thermal Barrier Coatings under the Synergistic Effect of Thermal Shock and CMAS Corrosion

Microstructure and High Temperature Wear of the Thermal Barrier Coatings on TiAl Alloys

Investigation of the failure mechanism of thermal barrier coatings prepared by electron beam physical vapor deposition

Investigation of Thermal Shock Behavior of Multilayer Thermal Barrier Coatings with Superior Erosion Resistance Prepared by Atmospheric Plasma Spraying

Al 2 O 3 -Modified 7YSZ Thermal Barrier Coatings for Protection Against Volcanic Ash Corrosion

Effect of Bionic Unit Shapes on Solid Particle Erosion Resistance of ZrO2–7wt%Y2O3 Thermal Barrier Coatings Processed by Laser

Solid particle erosion behavior of thermal barrier coatings produced by atmospheric plasma spray technique

Thermal barrier coatings with Al2O3–Pt composite bond-coat and La2Zr2O7–Pt top-coat prepared by cathode plasma electrolytic deposition

Effect of Bionic Unit Shapes on Solid Particle Erosion Resistance of ZrO 2 –7wt%Y 2 O 3 Thermal Barrier Coatings Processed by Laser